以不经压制的Mg、Ni混合粉末为原料,利用氢化燃烧合成法在合成温度850 K和1.8 MPa初始合成氢压下制备了镁基储氢合金氢化物Mg2NiH4,并利用XRD及PCT仪分析了其物相组成和储氢性能.研究表明,产物由单一物相Mg2NiH4组成,无未反应的Ni和不完全氢化的Mg2NiH0.3;相对于传统熔炼法制备的Mg2Ni,氢化燃烧合成产物具有更高的氢化活性,在没有任何活化处理的前提下,第一次吸氢就能以很快的速度达到饱和吸氢量,同时在任何吸氢温度下均具有较好的吸氢动力学性能,且随温度的降低,最大吸氢量降低幅度较小,平台压和吸放氢温度的关系为:lgP(0.1 MPa)=-3 187.6/ T+6.362 4(吸氢),lgP(0.1 MPa)=-3 468.4/T+6.694 3(放氢).
参考文献
| [1] | AKIYAMA Tomohiro;ISOGAI Hiromichi;YAGI Junichiro .Hydriding combustion synthesis for the production of hydrogen storage alloy[J].Journal of Alloys and Compounds,1997,252(1-2):L1-L4. |
| [2] | L.Q. Li;T. Akiyama .Effect of hydrogen pressure on the combustion synthesis of Mg2NiH4[J].Intermetallics,1999(2):201-205. |
| [3] | LI Li quan;AKIYAMA Tomohiro;YAGI Jun ichiro .Production of hydrogen storage alloys of Mg2NiH4 by hydriding combustion synthesis in laboratory scale[J].Journal of Materials Synthesis and Processing,2000,8:7-14. |
| [4] | Liquan Li;Tomohiro Akiyama;Jun-ichiro Yagi .Activity and capacity of hydrogen storage alloy Mg_2NiH_4 produced by hydriding combustion synthesis[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2001(1/2):118-123. |
| [5] | Tomohiro Akiyama;Toshimitsu Negishi;Katsushi Saito;Liquan Li;Jun-ichiro Yagi .Operating conditions for hydriding combustion synthesis of pure Mg{sub}2NiH{sub}4[J].Materials transactions,2001(8):1748-1752. |
| [6] | 胡子龙.贮氢材料[M].北京:化学工业出版社,2002 |
| [7] | Qian Li;Kuo-Chih Chou;Qin Lin;Li-Jun Jiang;Feng Zhan .Hydrogen absorption and desorption kinetics of Ag-Mg-Ni alloys[J].International journal of hydrogen energy,2004(8):843-849. |
| [8] | 巴志新,柳东明,李李泉.镁的氢化反应对氢化燃烧合成储氢合金Mg2NiH4纯度的影响[J].材料科学与工程学报,2004(04):539-543. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%