为了提高W-Cu复合材料的致密度,采用机械球磨-冷压制坯-液相烧结-热静液挤压-热处理工艺,制备出微观组织弥散分布、性能优异的W-35%Cu复合材料.采用扫描电镜、电子探针等测试手段分别对烧结及挤压后材料的组织及性能进行了分析.实验结果表明,采用机械球磨技术制备的W-35%Cu复合粉,经液相活化烧结后,再经热静液挤压进一步形变和致密,材料的硬度以及导电性能都有较大提高.在800℃真空热处理2 h后,获得了硬度高于200HB,电导率高于40m/Ω·mm2的W-35%Cu形变复合材料.
参考文献
| [1] | JEDMZIK R;NEUBRAND A;RODER J.Electrochemical processing and characterization of grade W-Cu composite[A].Reutte,1997:11-15. |
| [2] | 吕大铭.钨铜复合材料研究的新进展[J].中国钨业,2000(06):27-31. |
| [3] | 刘平;田保红;赵冬梅.铜合金功能材料[M].北京:科学出版社,2004 |
| [4] | BRYSKIN B;OHRINE E K.Processing of High-strength,High-conductivity W-Cu composite[A].Reutte,1997:358-370. |
| [5] | MOON I H.Sintering of mechanically alloyed nanostructured tungsten-copper alloys[J].Metal Powder Report,1998(10):38-41. |
| [6] | Jin-Chun Kim;Sung-Soo Ryu;Young Do Kim;In-Hyung Moon .Densification behavior of mechanically alloyed W-Cu composite powders by the double rearrangement process[J].Scripta materialia,1998(6):669-676. |
| [7] | LEE J S;KIM T H.Densification and Microstructure of the Nanocomposite W-Cu Powders[J].Nanostructured Materials,1995(06):691-694. |
| [8] | JOHNSON J L;GERMAN R M .Phase equilibria effect on enhanced liquid phase sintering of W-Cu[J].Metallurgical and Materials Transactions,1993,24(11):2369-2377. |
| [9] | JOHNSON J L;GERMAN R M .Chemically activatedliquid phase sintering of W-Cu[J].The international Joumal of Powder Metallurgy,1994,30(01):91-101. |
| [10] | IHN T H;LEE S W;JOO S K.Effect of Transitionmetal addition on liquid phase sintering of W-Cu[J].Powder Metallurgy,1994(04):283-288. |
| [11] | 刘京雷 .Cu-15wt﹪Cr粉末形变复合工艺及组织性能研究[D].哈尔滨工业大学,2003. |
| [12] | 于洋 .93W-4.9Ni-2.1Fe合金热变形强化与微观组织研究[D].哈尔滨工业大学,2005. |
| [13] | 杨成功 .W-35wt﹪Cu粉末复合材料制备新工艺研究[D].哈尔滨工业大学,2003. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%