为了研究粘接接头内胶粘剂的耐热性能,采用X射线能谱分析确定了不同条件下粘接接头内胶粘剂的元素组成及其变化行为,利用X射线能谱计算了胶粘剂的热失重率,进而计算出聚酰亚胺薄膜粘接接头内胶粘剂的热分解动力学,并与空气环境下胶粘剂热分解活化能进行了比较.计算结果表明,粘接接头内胶粘剂的热分解速率低于空气环境下胶粘剂热分解速率,这种分析测试方法为原位表征粘接接头内胶粘剂耐热性能提供了一种新的分析方法.
参考文献
[1] | KHMELNITSKII R A;LUKASHENKO I M;KALINKEVICH G A et al.Thermal degradation of phenol-formaldehyde binders of carbon-graphite materials[J].Solid Fuel Chemistry,1989,23(02):108-113. |
[2] | KURUMADA AKIRA;OKU TATSUO;KAWAMATA KIYOHIRO et al.Thermal shock resistances of a bonding material of C/C composites and copper[J].Transactions of the Japan Society of Mechanical Engineers,1997,63(04):794-800. |
[3] | JOANNIE W C;KHALED A;MICHAEL R et al.Effect of water,salt solution and simulated concrete pore solution on the properties of composite matrix resins used in civil engineering applications[J].Polymer Composites,2001,22:282. |
[4] | LIN Jiamin;MA Chenchim .Thermal degradation of phenolic resin/silica hybrid creamers[J].Polymer Degradation and Stability,2000,69:229-235. |
[5] | 刘伟昌,申胜军,王晓工,周其庠,刘德山.一种液晶环氧树脂固化中扩散控制动力学研究[J].高分子学报,2000(02):167-172. |
[6] | 高俊刚,李燕芳.双酚-S环氧树脂与琥珀酸酐固化反应动力学[J].物理化学学报,2000(05):405-409. |
[7] | 高俊刚,刘彦芳,王逢利.双酚-A型硼酚醛树脂的结构与热分解动力学的研究[J].高分子材料科学与工程,1995(05):31-35. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%