采用铜模吸铸法获得直径为2 mm的Fe61Co10Zr5W4B20块体非晶合金.采用X射线衍射、扫描电镜、示差扫描量热仪、微显硬度及压缩实验等研究了非晶合金的结构、热稳定性、显微硬度与压缩性能.结果表明:Mo的引入不利于非晶合金的形成;Fe61Co10Zr5W4B20块体非晶合金表现为二级晶化,玻璃转变温度为561.1℃,晶化起始温度为619.0℃,第一晶化峰值温度为632.6℃,第二晶化峰值温度为747.0℃,过冷液相区为57.9℃;该非晶合金的显微硬度为1207HV0.2,抗压强度σbc为1707.6 MPa.
参考文献
[1] | R. Hasegawa .Applications of amorphous magnetic alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(0):90-97. |
[2] | Akihisa Inoue;Yoshiyuki Shinohara;Jin Seon Gook .Thermal and Magnetic Properties of Bulk Fe-Based Glassy Alloys Prepared by Copper Mold Casting[J].Materials Transactions, JIM,1995(12):1427-1433. |
[3] | Inoue A;Zhang T;Takeuchi A .Bulk amorphous alloys with high mechanical strength and good soft magnetic properties in Fe-TM-B (TM=IV-VIII group transition metal) system[J].Applied physics letters,1997(4):464-466. |
[4] | T. D. Shen;R. B. Schwarz .Bulk ferromagnetic glasses prepared by flux melting and water quenching[J].Applied physics letters,1999(1):49-51. |
[5] | Akihisa Inoue;Akira Takeuchi;Baolong Shen .Formation and Functional Properties of Fe-Based Bulk Glassy Alloys[J].Materials transactions,2001(6):970-978. |
[6] | Yong Hu;Ming Xiang Pan;Lin Liu .Synthesis of Fe-based bulk metallic glasses with low purity materials by multi-metalloids addition[J].Materials Letters,2003(18):2698-2701. |
[7] | PAWLIK P;DAVIES H A;GIBBS M J .Magnetic properties and glass formability of Fe61 Co10 Zr5 W4 B20 bulk metallic glassy alloy[J].Applied Physics Letters,2003,83(14):2775-2777. |
[8] | Wang WH;Pan MX;Zhao DQ;Hu Y;Bai HY .Enhancement of the soft magnetic properties of FeCoZrMoWB bulk metallic glass by microalloying[J].Journal of Physics. Condensed Matter,2004(21):3719-3723. |
[9] | T. D. SHEN;R. B. SCHWARZ .BULK FERROMAGNETIC GLASSES IN THE Fe-Ni-P-B SYSTEM[J].Acta materialia,2001(5):837-847. |
[10] | 肖华星,陈光,孙强金.吸铸法制备Fe-基大块非晶合金[J].热加工工艺,2004(02):18-19,22. |
[11] | 陈非非,周少雄.Fe74Al4 Sn2(PSiBC)20块体非晶合金的制备与晶化研究[J].材料热处理学报,2004(03):5-9. |
[12] | Role of yttrium in glass formation of Fe-based bulk metallic glasses[J].Applied physics letters,2003(13):2581-2583. |
[13] | PONNAMBALAM V;POON S J;SHIFLET G J et al.Synthesis of iron -based bulk metallic glasses as nonferromagnetic amorphous steel alloys[J].Applied Physics Letters,2003,83(06):1131-1133. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%