为了研究在较低的温度下制备α-Al2O3纳米粉体工艺路线,以Al(NO3)3·9H2O和NH3·H2O溶液为原料,经改进的沉淀反应和原位诱导结晶,制备了分散性能良好的α-Al2O3纳米粉体.用XRD、TEM等技术研究了产物的物相、组成和形貌.结果表明,改进的沉淀反应和原位诱导结晶相结合,可有效的降低煅烧温度.在900℃煅烧2h,即可得到尺寸分布均匀,结晶性好,分散性能良好的α-Al2O3纳米粉体.NH4NO3的存在对于α相交具有明显的促进作用.
参考文献
[1] | 吴洁华,李包顺,郭景坤.二步煅烧法制备超细α-Al2O3粉[J].无机材料学报,1999(04):662. |
[2] | JANBEY A;PATl R K;TAHIR S et al.A new chemieal route for the synthesis of nano-crystalline α-Al2O3 powder[J].Journal of the European Ceramic Society,2001,21:2285-2289. |
[3] | 陈龙武.微乳液反应法制备氧化铝(含水)超细微粒[J].高等学校化学学报,1995(01):13. |
[4] | SHARMA P K;VARADAN V V;VARADAN V K .A critical role of pH in the colloidal synthesis and phase transformation ofllano size α-Al2O3 with high surface area[J].Journal of the European Ceramic Society,2003,23:659-666. |
[5] | 王宏志,高濂,李炜群,李强.高分子网络凝胶法制备纳米α-Al2O3粉体[J].无机材料学报,2000(02):356-360. |
[6] | Wen HL.;Yen FS. .Growth characteristics of boehmite-derived ultrafine theta and alpha-alumina particles during phase transformation[J].Journal of Crystal Growth,2000(1/4):696-708. |
[7] | M. Thiruchitrambalam;V.R. Palkar;V. Gopinathan .Hydrolysis of aluminium metal and sol-gel processing of nano alumina[J].Materials Letters,2004(24):3063-3066. |
[8] | 张增志,许海凤,张利梅.用异醇铝溶液燃烧化学沉积α-Al2O3纳米晶[J].材料科学与工程学报,2004(01):33-37. |
[9] | Hui-Ling Wen Yi-Yao Chen .Size characterization of θ-and α-AI2O3 crystallites during phase transformation[J].Nanostructured Materials,1999(1):89-101. |
[10] | 曾文明;陈念贻;归林华 等.无机盐制备氧化铝纳米粉及其物理化学的研究[J].无机材料学报,1998,13(06):887-892. |
[11] | 古堂生;林光明 .非晶态和晶态纳米氧化铝粉的相变与红外光谱[J].无机材料学报,1997,12(06):840-844. |
[12] | Yi-Quan Wu;Yu-Feng Zhang;Xiao-Xian Huang;Jing-Kun Guo .Preparation of platelike nano alpha alumina particles[J].Ceramics International,2001(3):265-268. |
[13] | 李月明,周健儿,顾幸勇,马光华.溶胶-凝胶法制备Al2O3纳米粉[J].中国陶瓷,2002(05):4-6. |
[14] | Frazee JW.;Harris TM. .Processing of alumina low-density xerogels by ambient pressure drying[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2001(1/3):84-89. |
[15] | 晏泓,张猛,陆路,许并社.Ni对纳米α-Al2 O3/Ni粉体中α相转变温度的影响[J].材料科学与工艺,2005(03):278-280. |
[16] | 杨晔,吴玉程,李勇,崔平.碳酸铝铵低温热分解制备α-Al2O3超细粉末[J].过程工程学报,2002(04):325-329. |
[17] | 李继光;孙旭东;张民 .碳酸铝铵热分解法制备α-Al2O3超细粉[J].无机材料学报,1998,13(06):803-807. |
[18] | SHIAU F S;FANG T T .Low-temperature synthesis of α-alumina using citrate process with α-alumina seeding[J].Materials Chemistry and Physics,1999,60(01):91-94. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%