为了改善铝合金的力学性能,利用形变和时效工艺提高Al-3.5Cu-1.5Li-0.12Zr合金的强度和塑性.采用TEM观察和室温拉伸试验等手段,研究了形变量和时效工艺对含钪Al-3.5Cu-1.5Li-0.12Zr合金微观组织与拉伸性能的影响.结果表明,时效前的变形能促进T1(Al2CuLi)相弥散细小析出,显著提高合金强度,使时效峰值提前.合金强度随形变量和时效时间增加而增加,到峰值后,随形变量增加和时效时间的延长,T1相长大粗化,合金强度和塑性降低.该合金合宜的形变量和时效工艺为3.5%预变形和160℃/24h时效.
参考文献
| [1] | K. S. KUMAR;S. A. BROWN;J. R. PICKENS .MICROSTRUCTURAL EVOLUTION DURING AGING OF AN Al-Cu-Li-Ag-Mg-Zr ALLOY[J].Acta materialia,1996(5):1899-1915. |
| [2] | DRITS A M;KRIMOVA T V.Aluminium-lithium alloys for aerospace[J].Current Advances in Materials and Processes,1998(06):48-51. |
| [3] | FRUDLIANDER I N;KABLOV E N;KOLOBNEV N I et al.Aluminum-base alloy and article made of it[P].RP 2163940,1999-09-08. |
| [4] | JOH C H;KAZUHIRO A;YASUHIRO M .Effect of Scaddition on coarsening behavior of Al3Li precipitates in Al-Li alloys[J].Materials Transactions,1998,5(40):439-443. |
| [5] | Y.V.Milman;O.i.Sirko .'Sc Effect' of improving mechanical properties in aluminium alloys[J].Materials Science Forum,2000(0):1107-1112. |
| [6] | TAN Cheng-yu,ZHENG Zi-qiao,XIA Chang-qing.The Aging Feature of Al-Li-Cu-Mg-Zr Alloy Containing Sc[J].中南工业大学学报,2000(02):65. |
| [7] | 夏德顺.含钪的铝和铝锂合金[J].航天工艺,1999(02):37-42. |
| [8] | 杨志强,尹志民.俄罗斯铝-钪合金的研究与开发[J].轻合金加工技术,2003(11):34-36,40. |
| [9] | 贾连锁,卫英慧,胡兰青,许并社.稀土元素Ce和预变形对Al-Li-Cu-Zr合金时效相变过程的影响[J].稀有金属材料与工程,2002(02):156-159. |
| [10] | 蒋呐,向曙光,郑子樵.CP276铝锂合金的应变时效工艺[J].中国有色金属学报,1999(04):694-699. |
| [11] | 刘斯仁 .预变形对CP276型Al-Li合金拉伸性能的影响[J].稀有金属,1997,7(04):311-314. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%