通过常温力学性能测试和透射电镜(TEM)研究了淬火速率对7055铝合金组织和力学性能的影响.结果表明,一定时效条件下,合金的力学性能随淬火速率降低而下降.组织观察发现,淬火速率小时,合金在冷却过程中于Al3Zr粒子和晶界非均匀形核析出粗大η平衡相,降低固溶体过饱和程度,削弱时效强化效果.时效时这些粗大η平衡相继续长大并在周围形成无沉淀析出带.晶界无沉淀析出带宽度随淬火速率降低而增大.对合金力学性能下降的原因进行了分析和探讨.
参考文献
| [1] | STARKE E A;STALEY J T .Application of modern aluminum alloys to aircraft[J].Progress in Aerospace Sciences,1996,32(2-3):131-172. |
| [2] | COLE G S;SHERMAN A M .Lightweight materials for automotive applications[J].Materials Characterization,1995,35:3-9. |
| [3] | WILLIAMS J c;STARKE Jr.E A .Progress in stmctural materials for aerospace systems[J].Acta Materialia,2003,51:5775-5799. |
| [4] | 陈康华,刘红卫,刘允中.强化固溶对7055铝合金力学性能和断裂行为的影响[J].中南工业大学学报(自然科学版),2000(06):528-531. |
| [5] | 郑子樵,李红英,莫志民.一种7055型铝合金的RRA处理[J].中国有色金属学报,2001(05):771-776. |
| [6] | I. N. Fridlyander .LAWS OF VARIATION OF PROPERTIES OF ALUMINUM ALLOYS DURING AGING[J].Metal Science and Heat Treatment,2003(9/10):337-340. |
| [7] | Deschamps A.;Brechet Y. .Influence of quench and heating rates on the ageing response of an Al-Zn-Mg-(Zr) alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):200-207. |
| [8] | THOMPSON D S;SUBRAMANYA B S;LEVY S A .Quench rate effects in Al-Zn-Mg-Cu alloys[J].Metallurgical and Materials Transactions,1971,2:1149-1160. |
| [9] | A. Deschamps;Y. Brechet .Nature and distribution of quench-induced precipitation in an Al-Zn-Mg-Cu alloy[J].Scripta materialia,1998(11):1517-1522. |
| [10] | BRYANT A J .The effect of composition upon the quench-sensitivity of some Al-zn-Mg alloy[J].Journal of the Institute of Metals,1966,94:94-99. |
| [11] | DUMONT D;DESCHAMPS A;BRECHET C et al.Characterization of precipitation microstructures in aluminium alloys 7040 and 7050 and their relationship to mechanical behavior[J].Journal of Materials Science and Technology,2004,20(05):567-576. |
| [12] | ENGLER O;SACHOT E;EHRSTREM J C .Recrystallisation and texture in hot deformed aluminium alloy 7010 thick plates[J].Journal of Materials Science and Technology,1996,12:717-729. |
| [13] | YAMAZAKI S;OTSUKA H;KIKUCHI T .Pefipheral-recrystallized structures formed in Al-Zn-Mg-Cu-Zr alloy materials during extrusion and their quenching sensitivity[J].Joumal of Materials Proceasing Technology,1993,38(04):689-701. |
| [14] | D. Godard;P. Archambault;E. Aeby-Gautier .Precipitation sequences during quenching of the AA 7010 alloy[J].Acta materialia,2002(9):2319-2329. |
| [15] | VASUDEVAN A K;DOHERTY R D .Grain Boundary Ductile Fracture In Precipitation Hardened Aluminum Alloys[J].ACTA METALLURGICA,1987,35(06):1193-1219. |
| [16] | PORTER D A;EASTERLING K E.Phase transformation in metals and alloys[M].Britain,Alden Press,Oxford,1981 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%