采用BN替代碳质材料,研究BN对IF钢连铸保护渣理化性能的影响,在此基础上设计开发出IF钢新型连铸保护渣.新型连铸保护渣在熔化特性、粘性特征、夹杂物吸收能力和结晶性能等方面与传统连铸保护渣十分接近.新型骨架粒子BN可以使连铸保护渣熔化温度、熔化速度、粘度和结晶温度减小、Al2O3吸收速率增大.采用新型连铸保护渣可以彻底解决IF钢的结晶器内增碳问题,不会发生IF钢增硼问题,而在非稳态浇注条件下可能发生增硼反应.
参考文献
[1] | Bommaraju R.Optimum selection and application of mold fluxes for carbon steels[A].Washington:ISS,1991:131-146. |
[2] | Pinheiro C A;Samarasekera I V;Brimacombe J K .Mold fluxes for continuous casting of steel[J].Ironmaking and Steelmaking,1995,22(04):45-47. |
[3] | Nakano T;Takeuchi S;Fujji T.Charateristics of new mold fluxes for strand casting of low and ultra low carbon steel slabs[A].Washington:ISS,1991:639-646. |
[4] | Skoczylas G.Recent developments in high viscosity mold powders for TiSULC steel grades[A].Chicago:ISS,1995:269-275. |
[5] | Kusano A;Sato N;Okimori M.Improvement of mold fluxes for stainless and titanium bearing steels[A].Washington:ISS,1991:147-151. |
[6] | Terada S;Kaneko S;Ishikawa T.Research of substitution for carbon (Development of mold fluxes for ultra-low-carbon steel)[A].Washington:ISS,1991:635-638. |
[7] | 山崎達也;石井正司 .用途開発の進むボロンナイトライ[J].金属(日本),1970,19(01):85-88. |
[8] | 刘承军,姜茂发.连铸保护渣的绝热保温性能[J].钢铁研究学报,2002(03):1-4. |
[9] | Takeuchi H;Morl H;Nishida T et al.Development of a carbon-free casting powder for continuous casting of steels[J].ISIJ International,1979,19(03):274-282. |
[10] | 饶东生.硅酸盐物理化学[M].北京:冶金工业出版社,1991:53-68. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%