采用电化学、光电化学和交流阻抗等方法研究了氢对纯铁钝化膜形成过程和电子性质的影响.结果表明氢的存在会延长钝化膜的形成,增加稳态钝化条件下的溶解速率;氢能提高钝化膜光电流、降低禁带宽度;氢促使钝化膜的电容和掺杂浓度升高,并降低膜的平带电位.
参考文献
[1] | 褚武扬.氢损伤与滞后断裂[M].北京:冶金工业出版社,1988 |
[2] | Haseawa M;Osawa M .Anomalous corrosion of austentic stainless steel exposed at high temperature and pressure[J].Corrosion,1980,36:67. |
[3] | 乔利杰;缪辉俊;褚武扬.氢、应力和腐蚀三者对奥氏体不锈钢的协同作用[J].中国科学A辑,1996(12):1218. |
[4] | 胡小丽;黄震中;乔利杰;褚武扬 .氢和应力对阳极溶解的影响[J].中国腐蚀与防护学报,1996,16:187. |
[5] | Chu W Y;Liu T W;Hsiao C M .Mechanism of SCC of steel in H2S[J].Corrosion,1981,16:320. |
[6] | 乔利杰;徐荣杰;褚武扬;肖纪美 .氢对黄铜应力腐蚀开裂敏感性的影响[J].中国腐蚀与防护学报,1995,15:61. |
[7] | Murphy O J;Bockris J O .SIMS evidence concerning water in passive layer[J].Journal of the Electrochemical Society,1982,129:2149. |
[8] | Boniface A O;Welwille B N .Kinetics of formation of passive oxide films on corrosion-resistant Fe-Cr thin films[J].Journal of the Electrochemical Society,1984,131:234. |
[9] | Murphy O J;Pou T E;Bockris J O M;Tongson L L .Investigation of the anodically formed passive film on iron by secondary ion mass spectroscopy[J].Journal of the Electrochemical Society,1984,131:2785. |
[10] | 乔利杰;曾一民;褚武扬 .氢对310不锈钢点蚀敏感性的影响[J].中国腐蚀与防护学报,1998,15:61. |
[11] | Frelicher M;Goff A;Jovancicevic V.[A].Amsterdam Elsevier,1983:477. |
[12] | Tsuru T;Haruyama S .[J].Journal of the Japan Institute of Metals,1986,27:382. |
[13] | 吴浩青.电化学动力学[M].北京:高等教育出版社,1998 |
[14] | PyunSu-Il;Lim C;Oriani R A .The role of hydrogen in the pitting of passivating films on pure iron[J].Corrosion Science,1992,33:437. |
[15] | Gerischer H .Models for the discussion of the photo-electrochemical response of oxide layers on metals[J].Corrosion Science,1989,29:257. |
[16] | Schmuki P;Bohni H .A photo-electrochemical investigation of passive film formed by alternating voltage passivation[J].Journal of the Electrochemical Society,1993,140:L119. |
[17] | Feller H G;Vhilg H H .Relation of electron configuration to passivity in Cr-Ni-Fe alloys[J].Journal of the Electrochemical Society,1960,107:864. |
[18] | Kedden M;Mahos O S;Takenouti H .Reaction model for iron dissolution studied by electrode impedence[J].Journal of the Electrochemical Society,1981,128:257. |
[19] | 曾一民;乔利杰;褚武扬 .氢对310不锈钢钝化膜的影响[J].中国腐蚀与防护学报,1999,19(04):233. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%