利用旋转圆盘式冲刷腐蚀试验装置，研究了不同固化度的SEBF-2型熔融结合环氧粉末涂层在1％NaCl+1％金刚砂砂浆中的冲蚀特性，并观察了涂层表面形貌．实验结果表明：对不同条件固化的试样，固化度越高，抗冲蚀性能越好．固化度相同而固化工艺不同时，涂层的冲蚀性能存在一定的差异，高温短时间固化涂层不如低温长时间固化涂层耐冲蚀，这与其交联结构密切相关．
The erosion resistance of SEBF-2 fusion-bonded epoxy powder coatings with different curingdegrees has been studied in 1wt % NaCl + 1wt % emery sand slurry by using rotating disk rig. The cross-linking density and structure of the coatings were analyzed by measuring DOC (degree of curing), Tg andwater absorption. The surface morphology of the coatings was observed by SEM. The results showed thatthe erosion resistance of the coatings increased with the curing degree. The cratings with the same curingdegree cured by different curing processes had different erosion resistances. The erosion resistance of thecoating cured at low temperature for long time was superior to that of the coating cured at high ~turefor short time. The mechanism of above phenomena was elucidated in term of cross-linking density andstructure.
参考文献
| [1] | Yoshiro Iwai;Kazuyuki Nambu .Slurry wear properties of pump lining materials[J].Wear,1997,210:211-219. |
| [2] | Zhang J X;Richardson M O W;Wilcox G D et al.Assessment of resistance of noometallic cratings to silt abrasion and cavitationerosion in a rotating disk test rig[J].Wear,1996,194:149-155. |
| [3] | Parslow G I;Stephenson D J;Strutt J E et al.Paint Iayer erosion resistance behavior for use in a multilayer paint erosion indicationtechnique[J].Wear,1997,212:103-109. |
| [4] | 张剑新.颗粒填料增强环氧树脂在水利机械表面保护层上的应用研究[J].玻璃钢/复合材料,1993(05):21-26. |
| [5] | 马向东;林福严;邵荷生.耐磨胶粘涂层在浆体冲蚀条件下的研究[J].润滑与密封,1991(04):11-15. |
| [6] | Schwalm R.;Reich W.;Beck E.;Enenkel P.;Menzel K.;Haussling L. .TUNING THE MECHANICAL PROPERTIES OF UV COATINGS TOWARDS HARD AND FLEXIBLE SYSTEMS[J].Progress in Organic Coatings: An International Review Journal,1997(1/4):191-196. |
| [7] | Masaki Shimbo;Mitsukazu Ochi;Katsumasa Arai .Internal stress of cured epoxide resin coatings having different network chains[J].Journal of Coatings Technology,1984,56(713):45-51. |
| [8] | 郑玉贵.液/固双相流冲刷腐蚀实验装置的研制及动态电化学测试[J].腐蚀科学与防护技术,1993(04):286. |
| [9] | TURENNE S;Chatigny Y;Simard D et al.The effect of abrasive particle size on the slurry erosion resistance of particulate-reinforcedaluminium alloy[J].WEAR,1990,141:147-158. |
| [10] | Lunak S;Vladyka J et al.Effectof diffusion control in theglass transition region on critical conversion at thegel point during curingof epoxy resins[J].Polymer,1978,19:931-933. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%