设计了一套适合于研究金属材料在薄层液膜下腐蚀的三电极电化学测量电池.Cl-浓度的增大,促进了Zn在大量溶液中的阳极反应,降低了传递电阻和自腐蚀电位,从而导致腐蚀速率增大.在0.01 mol/L的NaCl溶液中,随着液膜厚度的减小,传递电阻增大,腐蚀速度降低.在同浓度、不同电解质的大量溶液中,Na2SO4溶液对Zn的腐蚀最严重,其次是NaNO3,腐蚀最轻的是NaCl;而在薄层液膜下,对Zn的腐蚀作用最明显的是NaCl;其次是Na2SO4;再次是NaNO3,最轻的是Na2CO3.
参考文献
| [1] | Cox A;Lyon S B .An electrochemical study of the atmospheric cor rosion of mild steel Ⅰ experimental[J].Corrosion Science,1994,36(07):1167-1176. |
| [2] | Fiaud C;Keddam M;Kadri A;akenouti H .Electrochemicalimpedance in a thin surface electrolyte layer influence of the poten tial probe location[J].Electrochimica Acta,1987(32):445-448. |
| [3] | 张学元,柯克,杜元龙.金属在薄层液膜下电化学腐蚀电池的设计[J].中国腐蚀与防护学报,2001(02):117-122. |
| [4] | KEDDAM M;Hugot Le;Goff A;Takenouti H, et al.The influence of a thin electrolyte layer on the corrosion process of zinc in chloride containing solutions[J].Corrosion Science,1992,33(08):1243. |
| [5] | Xiaoge Gregory Zhang.Corrosion and Electrochemistry of Zinc[M].New York: Plenum Press,1996:157. |
| [6] | 王凤平 .大气CO<,2>浓度升高对金属大气腐蚀的影响[D].中国科学院金属研究所,2000. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%