采用慢应变速率试验(SSRT)研究了不同电位下X70管线钢在近中性pH溶液中的应力腐蚀破裂(SCC)行为,同时研究了溶液中通入不同含量CO2对SCC的影响.结果表明,X70管线钢在近中性pH溶液中的开裂方式是穿晶型的,具有准解理特征,并且随着外加阴极电位的降低,SCC敏感性增加;随CO2含量的增加,pH值降低,SCC敏感性增加.均表现为氢致开裂占主导.
参考文献
[1] | 郭浩,蔡殉,杨武.影响管线钢应力腐蚀破裂的力学和材料因素[J].机械工程材料,2002(04):1-5,10. |
[2] | J.G. Gonzalez-Rodriguez;M. Casales;V.M. Salinas-Bravo .Effect of Microstructure on the Stress Corrosion Cracking of X-80 Pipeline Steel in Diluted Sodium Bicarbonate Solutions[J].Corrosion: The Journal of Science and Engineering,2002(7):584-590. |
[3] | Rebak R B;Xia Z;Safruddin R;Szklarska- Smialowska Z .Effect of solution composition and electrochemical potential on stress corrosion cracking of X- 52 pipeline steel[J].Corrosion,1996,52(05):396-405. |
[4] | Kushida T;Nose K;Asahi H.Effects of metallurgical factors and test conditions on near neutral Ph SCC of pipeline steels[A].Houston,NACE International TX,2001:01213. |
[5] | W. Chen;F. King;E. Vokes .Characteristics of Near-Neutral-pH Stress Corrosion Cracks in an X-65 Pipeline[J].Corrosion: The Journal of Science and Engineering,2002(3):267-275. |
[6] | Parkins R N;Blanchard W K Jr;Delanty B S .Transgranular stress corrosion cracking of high - pressure pipelines in contact with solutions of near neutral pH[J].Corrosion,1994,50(05):394-408. |
[7] | B. Gu;J. Luo;X. Mao .Hydrogen-facilitated anodic dissolution-type stress corrosion cracking of pipeline steels in near-neutral pH solution[J].Corrosion: The Journal of Science and Engineering,1999(1):96-106. |
[8] | M. Puiggali;S. Rousserie;M. Touzet .Fatigue Crack Initiation on Low-Carbon Steel Pipes in a Near-Neutral-pH Environment Under Potential Control Conditions[J].Corrosion: The Journal of Science and Engineering,2002(11):961-970. |
[9] | B. Gu;W. Z. Yu;J. L. Luo;X. Mao .Transgranular stress corrosion cracking of X-80 and X-52 pipeline steels in dilute aqueous solution with near-neutral pH[J].Corrosion: The Journal of Science and Engineering,1999(3):312-318. |
[10] | Chen W X;Wang S H;King Fraser;Jack Tom R, Wilmott Martyn J.Hydrogen permeation behavior of X - 70 pipeline steel in a near-neutral pH soil environment[A].ASME,2000:953-960. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%