研究了流动条件下CO2分压、流速、原油含水率、溶液Cl-浓度及pH值对3种油套管常用材料N80、P105和SM110腐蚀行为的影响.90℃、1.5m/s时,随CO2分压升高,材料的腐蚀速率先升后降,在CO2分压为2.5MPa时,除N80钢外,其它材料的腐蚀速率达到最大值;90℃、CO2分压为2.5MPa时,随着流速的增加,腐蚀速率先升后降,在流速为1.5m/s时,材料的腐蚀速率达到最大值;原油含水率对材料的腐蚀速率影响较大;溶液的pH值及Cl-浓度对材料的腐蚀速率影响不明显.
参考文献
| [1] | 李建平,赵国仙,王玉,黄瑞祥,郝士明.塔里木油田用油套管钢的静态腐蚀研究[J].中国腐蚀与防护学报,2004(04):230-233. |
| [2] | Carlos A;Palacios T.Application of simulation of techniques for internal corrosion prediction[A].Houston:NACE,1997:2. |
| [3] | Nesi S;John P;Vrhova M .CO2 corrosion of carbon steel-from mechanism to empirical modelling[J].Corrosion Reviews,1997,15:112-126. |
| [4] | Gray L G S.Mechanism of carbon steel corrosion in brines containing dissolved carbon dioxide at Ph4[A].Houston:NACE,1989:464. |
| [5] | Gray L G S.Effect of pH and temperature on the mechanism of carbon steel[A].Houston:NACE,1998:40. |
| [6] | Vera J R.Flow Velocity Effect on CO2 Corrosion of Carbon Steel Using a Dynamic Field Tester[M].London:Europe Corrosion Federation,1994:94-119. |
| [7] | 张学元;邸超;雷良才.二氧化碳腐蚀与控制[M].北京:化学工业出版社,2000:57. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%