研究了X70钢在磷酸盐缓冲溶液中的亚稳态与稳态孔蚀的电化学行为特征.发现Cl-浓度对X70钢在磷酸盐缓冲溶液中的孔蚀保护电位影响不大,而PO3-4对X70钢有较强的孔蚀抑制作用,增加PO3-4浓度,能够有效提高X70钢的孔蚀保护电位.提高缓冲溶液的pH值能够抑制X70钢小孔的形核和生长.X70钢亚稳态小孔形核主要受到铝氧夹杂物的影响,且随着电位的升高,电流波动频率先升后降,而峰值电流则趋于增大.X70钢在磷酸盐缓冲溶液中形成的钝化膜在钝化区内阻抗基本不受电位的影响.
参考文献
| [1] | Frankel G S;Stockert L;Hunkeler F et al.Metastable pitting of stainless steel[J].CORROSION,1987,43(07):429-436. |
| [2] | Pistorius P C;Burstein G T .Growth of corrosion pits on stainless steel in chloride solution containing dilute sulphate[J].Corrosion Science,1992,33(12):1885-1897. |
| [3] | Pistorious P C;Burstein G T .Aspects of the effects of electrolyte composition on the occurrence of metastable pitting on stainless steel[J].Corrosion Science,1994,36(03):255-261. |
| [4] | Y. F. Cheng;J. L. Luo .Metastable pitting of carbon steel under potentiostatic control[J].Journal of the Electrochemical Society,1999(3):970-976. |
| [5] | Cheng Y F;Wilmott M;Luo J L .Analysis of the role of electrode capacitance on the initiation of pits for A516 carbon steel by electrochemical noise measurements[J].Corrosion Science,1999,41:1245-1256. |
| [6] | 董泽华,郭兴蓬,郑家燊,许立铭.用电化学噪声研究16Mn钢的亚稳态孔蚀特征[J].腐蚀科学与防护技术,2001(04):195-198. |
| [7] | Tang YM;Zuo Y .The metastable pitting of mild steel in bicarbonate solutions[J].Materials Chemistry and Physics,2004(1):221-226. |
| [8] | Fujioka E;Nishihara H;Aramaki K .The inhibition of pit nucleation and growth on the passive surface of iron in a borate buffer solution coataining Cl-by oxidizing inhibitors[J].Corrosion Science,1996,38(11):1915-1933. |
| [9] | G.T. Burstein;P.C. Pistohus .Surface Roughness and the Metastable Pitting of Stainless Steel in Chloride Solutions[J].Corrosion: The Journal of Science and Engineering,1995(5):380-385. |
| [10] | 王虎,左禹,毛健鹏.工业纯铁在NaNO2+NaCl溶液中的亚稳态孔蚀及其腐蚀形貌[J].北京化工大学学报(自然科学版),2004(05):41-44. |
| [11] | 魏宝明;郝凌 .几种非正半圆交流阻抗图谱的物理意义[J].全面腐蚀控制,1990,4(03):9-15. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%