采用固体法硼稀土共渗,研究了加稀土对渗层抗熔锌腐蚀性能的影响.结果表明,加入稀土后渗层抗熔锌腐蚀能力比不加稀土的提高3倍.主要原因是加入稀土后渗层致密、成分均匀、缺陷少、组织韧性好、裂纹扩展阻力大,致使裂纹不易扩展,难以形成锌蚀通道,从而材料的抗熔锌腐蚀能力增强.
参考文献
| [1] | 王桂新,韩文祥.渗硼层耐锌液腐蚀性的研究[J].河北工业大学学报,2001(05):79-84. |
| [2] | 曹晓明,温鸣,刘亚青.耐熔锌腐蚀材料及热镀锌内加热技术[J].中国机械工程,2002(19):1642-1645. |
| [3] | Tsipas D N;Triantafyllidis G K .Degradation behaviour of boronized carbon and high alloy steels in molten aluminum and zinc[J].Materials Letters,1998,37(03):128-131. |
| [4] | 谷志刚;刘竹风;白虹.渗硼低碳钢在热镀锌液中的耐蚀性[J].金属热处理,1998(04):12-14. |
| [5] | Gerd B .A study on morphology of boronized specimen[J].Crystal Research and Technology,1985,20(08):1085-1090. |
| [6] | Xia YQ.;Liu WM.;Yu LG.;Han N.;Xue QH. .Investigation on the tribological properties of boron and lanthanum permeated mild steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):17-23. |
| [7] | 刘瑞岩,王旭,张俊善,王秀敏,祝美丽.Effect of borate coating on corrosion resistance of pure nickel in molten LiCl-Li2O[J].中国有色金属学会会刊(英文版),2004(01):143-147. |
| [8] | 刘长禄;王丽风 .硼稀土粉末共渗及渗层的性能[J].金属热处理,1989,32(08):21-23. |
| [9] | 陶小克,董桂霞,彭日升,孙永昌.固体法稀土硼钒共渗的研究[J].中国稀土学报,2001(02):178-181. |
| [10] | 沈思雯,宋月鹏,冯承明.稀土元素对渗硼层显微硬度、耐磨性能的影响[J].山东农机,2002(05):13-15. |
| [11] | 宋月鹏,许斌,华磊,冯承明.Cr及RE元素对硼化物层脆性的影响[J].理化检验-物理分册,2000(05):203-206. |
| [12] | 艾云龙,王伟兰,程玉桂,刘长虹.45钢高、低温硼稀土粉末共渗层组织与性能分析[J].金属热处理,2004(02):34-36. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%