采用盐水滴腐蚀试验、腐蚀产物SEM及XPS分析、极化曲线测试分别研究了Ce3+和La3+对碳钢在NaCl溶液中的缓蚀机理,并利用热力学数据绘制了Ce-H2O及La-H2O二元电位-pH相图.结果表明,Ce3+和La3+能够在pH值较高的阴极区沉淀,阻碍O及电子在碳钢表面和溶液之间的转移和传递,通过抑制阴极反应从而减缓腐蚀的进行.热力学计算及电位-pH图表明Ce3+在有氧时可被氧化成沉淀倾向更强的Ce4+,在酸性溶液中Ce4+化合物的稳定性要高于La3+化合物,因此Ce3+的缓蚀效果要好于La3+.
参考文献
| [1] | Hinton B R W;Arnott D R;Ryan N E .The inhibition of aluminum alloy corrosion by cerium cations[J].Meter Forum,1984,7(04):211-217. |
| [2] | Hinton B R W .Cerium conversion coating for the corrosion protection of aluminum[J].Materials Forum,1986,9(03):162-173. |
| [3] | Arnott D R .Cationic film forming inhibitors for the corrosion protection of AA7075 aluminum alloy in chloride solutions[J].Materials Performance,1987,26(08):42-47. |
| [4] | Arnott D R .Cationic film forming inhibitors for the protection of AA7075 aluminum alloy against corrosion in aqueous chloride solutions[J].CORROSION,1989,45(01):12-19. |
| [5] | Goldie B P F;McCarroll J J .Inhibiting metal corrosion in aqueous systems[P].AU 3294784,1984. |
| [6] | 刘伯生.铝及铝合金上铈转化膜的研究[J].材料保护,1992(05):16. |
| [7] | 李久青;卢翠英;高陆生 等.铝合金表面稀土铈耐蚀膜[J].北京科技大学学报,1995,17(06):584-589. |
| [8] | 于兴文;周德瑞;尹钟大 等.铝合金表面三价稀土钝化膜的研究[J].中国有色金属学报,1999,9(01):73-78. |
| [9] | 方景礼;王济奎;刘琴 等.碳钢表面稀土转化膜的XPS和AES研究[J].中国稀土学报,2001,12(01):38-41. |
| [10] | 李国强,李荻,李久青,郭宝兰,彭明霞.铝合金阳极氧化膜上阴极电解沉积的稀土铈转化膜[J].中国腐蚀与防护学报,2001(03):150-157. |
| [11] | 顾宝珊,刘建华,纪晓春.铈盐对铝合金的缓蚀机理研究[J].中国腐蚀与防护学报,2006(01):53-58. |
| [12] | Rajendran N;Nishimura T.Monitoring of pH and chloride ion with in the rust of low alloy steels under atmospheric corrosion environment[A].上海,2004:425-428. |
| [13] | 梁英教;车荫昌;刘晓霞.无机物热力学数据手册[M].沈阳:东北大学出版社,1994 |
| [14] | 吴维昌;冯洪清;吴开治.标准电极电位数据手册[M].北京:科学出版社,1991 |
| [15] | 印永嘉.物理化学简明手册[M].北京:高等教育出版社,1988 |
| [16] | 杨德钧;沈卓身.金属腐蚀学[M].北京:冶金工业出版社,1999 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%