用极化曲线和交流阻抗等电化学方法研究了B510L热轧钢板表面氧化膜对基体钢板腐蚀行为的影响.结果表明:热轧钢板的阳极与阴极过程主要通过氧化膜自身缺陷在基体表面进行,氧化膜本身主要对基体金属起到物理屏蔽作用,并不影响膜下金属腐蚀反应的过程和机制.研究中发现腐蚀电流与氧化膜中存在的缺陷数量成正比,因此,氧化膜的孔隙率可以用有膜和无膜金属腐蚀电流比值表达.计算结果表明,测定氧化膜覆盖金属的腐蚀电流和极化电阻可以合理评价热轧钢板表面氧化膜的孔隙率.
参考文献
| [1] | 杨春征,李龙,丁桦,杜林秀,刘相华,王国栋,宋红梅,张丕军.控轧控冷工艺对B510L组织性能的影响[J].材料与冶金学报,2003(03):223-226. |
| [2] | Singh Raman R K .Laser Raman spectroscopy:a technique for rapid characterisation of oxide scale layers[J].Journal of Materials Science and Technology,1998,14(04):373-375. |
| [3] | Chen RY;Yuen W Y D .Review of the high temperature oxidation of iron and carbon steels in air and oxygen[J].Oxidation of Metals,2003,59(04):433-468. |
| [4] | Schutze M .An approach to a global model of the mechanical behaviour of oxide scales[J].Materials at High Temperatures,1994,12(03):237-247. |
| [5] | Tiley J;Zhang Y;Lenard J G;Hot c .ompression testing of mild steel industrial reheat furnace scale[J].Steel Research International,1999,70(04):437-440. |
| [6] | Sun W H;Tieu A K;Jiang Z Y et al.High temperature oxide scale characteristics of low carbon steel in hot rolling[J].Journal of Materials Processing Technology,2004,155-166(10):1300-1306. |
| [7] | 曹楚南.腐蚀电化学原理[M].北京:化学工业出版社,2004 |
| [8] | GB/T 4334.5-2000.GB/T 4334.5-2000.不锈钢硫酸-硫酸铜腐蚀实验方法[S].北京:国家质量技术监督局,2000. |