用直读光谱仪、万能材料试验机、光学显微镜、扫描电子显微镜等分析手段,分析高速列车7020铝合金车钩梁多处开裂现象及其原因.结果表明,开裂的7020铝合金车钩梁材料质量正常,服役后的车钩梁基体表面存在腐蚀坑,腐蚀坑中存在Cl-离子,主裂纹位于焊接热影响区和母材交界处,裂纹沿晶扩展.实验室采用和车钩梁相似的环境和受力状况进行模拟试验,高强度合金双悬臂梁试样的应力腐蚀开裂(SCC)裂纹形貌特征和车钩梁裂纹吻合良好,表明车钩梁开裂原因为SCC,并讨论了铝合金的SCC机理.
参考文献
| [1] | 姚曙光,许平.高速磁浮列车车体国产化[J].交通运输工程学报,2004(02):40-44. |
| [2] | Gur C H;Yid Z I .Nondestructive investigation on the effect of precipitation hardening on impact toughness of 7020 Al-Zn-Mg alloy[J].Materials Science and Engineering,2004,A382:95-400. |
| [3] | Song RG;Dietzel W;Zhang BJ;Liu WJ;Tseng MK;Atrens A .Stress corrosion cracking and hydrogen embrittlement of an Al-Zn-Mg-Cu alloy[J].Acta materialia,2004(16):4727-4743. |
| [4] | Liu J;Kulak M .A new parading in the design of aluminum alloy for aerospace applications[J].Materials Science Forum,2000,331-337:127-140. |
| [5] | Heinz A;Haszler A;Keidel C .Recent development in aluminium alloy for aerospace applications[J].Materials Science and Engineering,2000,A280(01):102-107. |
| [6] | 张晓云,孙志华,刘明辉,汤智慧,李斌.环境对高强度铝合金应力腐蚀行为的影响[J].中国腐蚀与防护学报,2007(06):354-362. |
| [7] | 孙志华,刘明辉,张晓云,高健,陆峰,汝继刚.时效制度对Al-Zn-Mg-Cu铝合金应力腐蚀敏感性的影响[J].中国腐蚀与防护学报,2006(04):232-236. |
| [8] | Burleigh T D .Mechanism of stress corrosion cracking for aluminum alloy(2)1980～1989 document summary[J].Corrosion,1991,47(02):89-98. |
| [9] | 刘继华,李荻,张佩芬.氢对LC4高强铝合金应力腐蚀断裂的影响[J].中国腐蚀与防护学报,2002(05):308-310. |
| [10] | Parkins R N;Yang W.Stress Corrosion Cracking,in Uhlig's Corrosion Handbook[M].北京:化学工业出版社,2005:525. |
| [11] | 褚武扬;乔利杰;陈奇志.断裂与环境断裂[M].北京:科学出版社,2001:120. |
| [12] | Hollingsworth E H;Hunsticker H Y .Corrosion of aluminum and aluminum alloys[J].CORROSION,1987,43(09):583-609. |
| [13] | 刘洋.铝合金应力腐蚀开裂的研究进展[J].北京联合大学学报（自然科学版）,2006(01):31-35,44. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%