针对9310钢研究了试验参数对疲劳小裂纹门槛值测试结果的影响.结果表明,对于9310高强钢采用恒Kmax/升Kmin方法进行小裂纹门槛值试验时,规范化的应力强度因子梯度CK和Δα值的选取对门槛值的影响很小.当Kmax在线弹性范围内选取时,由于裂尖过程区的断裂机制未发生变化,Kmax的选取对门槛值测试结果也基本没有影响.
参考文献
[1] | KITAGAWA H;TAKAHASHI S.Applicability of fracture mechanics to very small cracks or cracks in the early stage[A].OH,USA:Metals Park,SASM International,1976:627-631. |
[2] | MILLEER K J.A historical perspective of the important parameters of metal fatigue; and problems for the next century[A].北京:高等教育出版社,1999:15-39. |
[3] | MINAKAWA K;NEWMAN Jr J C;McEVILY A J .A critical study of the crack closure effect on near-threshold fatigue crack growth[J].Fatigue & Fracture of Engineering Material & Structure,1983,6(04):359-365. |
[4] | 吴学仁;NEWMAN Jr J C.高强度铝合金的小裂纹效应[A].北京:航空工业出版社,1994 |
[5] | HERMAN W A;HERTZBERG R W;JACCARD R .A simplified laboratory approach for the prediction of short crack behavior in engineering structures[J].Fatigue & Fracture of Engineering Material & Structure,1988,11(04):303-320. |
[6] | PRIDDL E K .The influence of test variables on the fatigue crack growth threshold[J].Fatigue & Fracture of Engineering Material & Structure,1989,12(04):333-345. |
[7] | CLARK T R;HERMAN W A;HERTZBERG R W et al.The influence of the K gradient and Kcmax level on fatigue response during the Kcmax threshold testing of Van 80 steel and Astroloy[J].International Journal of Fatigue,1997,19(02):177-182. |
[8] | NEWMAN J A;RIDDELL W T;PIASCIK R S.Effect of Kmax on fatigue crack growth threshold in aluminum alloys[A].West Conshohocken:American Society for Testing and Materials,PA,1999 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%