应用硅烷偶联剂(SG-Si900)烷烃链的空间位阻效应,以SG-Si900、钛酸丁酯和正硅酸乙酯(TEOS)为主要原料,经水解、恒温缩聚、蒸馏等工艺,合成钛-硅烷复合功能树脂,然后将树脂用水稀释,采用提拉法在玻璃表面制备超级亲水性薄膜;研究了SG-Si900/TEOS、硅钛摩尔比、复合树脂粘度、涂膜次数、固化温度等因素对薄膜亲水性能的影响,及薄膜的紫外线照射行为和波长在200~800nm范围内薄膜的透光率,并应用扫描电子显微镜研究了薄膜表面的微观结构和薄膜断层厚度.结果表明,制备复合树脂超亲水薄膜最佳工艺条件为:当硅钛摩尔比为9,SG-Si900/TEOS为1时,制备的钛硅烷复合超亲水性树脂经3次涂膜,200℃,1h固化,可形成与水接触角为0°的超级亲水薄膜,膜厚约为80nm.
参考文献
[1] | Wang R;HASHIMOTO K;FUJISHIMA A et al.Light induced amphiphilic surface[J].NATURE,1997,338:431-432. |
[2] | Fujishima A;RAO T N;TRYK D A .Titanium dioxide photocatalysis[J].Journal of Photochemistry and Photobiology C:Photochemistry Reviews,2000,1:1-27. |
[3] | T. Watanabe;A. Nakajima;R. Wang;M. Minabe;S. Moizumi;A. Fujishima;K. Hashimoto .Photocatalytic activity and photoinduced hydrophilicity of titanium dioxide coated glass[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1999(12):260-263. |
[4] | Ikezawa S.;Kubota T.;Suzuki R.;Koh S.;Mutuga F.;Yoshioka T.;Nishiwaki A.;Ninomiya Y.;Takahashi M.;Baba K.;Kida K.;Hara T. Famakinwa T.;Homyara H. .Applications of TiO2 film for environmental purification deposited by controlled electron beam-excited plasma[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2001(2):173-176. |
[5] | Yu J;ZHAO X .Effect of surface treatment on the photocatalytic activity and hydrophilic property of the sol-gel derived TiO2 thin films[J].Materials Research Bulletin,2001,6(06):97-107. |
[6] | 刘平,凌岚,林华香,付贤智.光催化抗雾膜材料的制备及其亲水性研究[J].高等学校化学学报,2000(03):462-465. |
[7] | Collino R;Therasse J et al.Biological activity of functionalized SiO2 thin films prepared by sol-gel method[J].Journal of Sol-Gel Science and Technology,1996,7(01):281-85. |
[8] | 余家国,赵修建,林立,韩建军,赵青南.超亲水TiO2/SiO2复合薄膜的制备与表征[J].无机材料学报,2001(03):529-534. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%