采用低压气相沉积法,在镍基高温合金DD32上制备铝化物涂层.涂层外层为β-NiAl,内层(扩散层)宽度接近外层,富集Re.在900℃,1000℃氧化500小时后,表面氧化膜为致密的α-Al2O3 和针状的θ-Al2O3,氧化动力学基本符合抛物线规律.氧化后的铝化物涂层外层为β-NiAl,有贫Al的Ni3Al沿晶界析出;内层(扩散层)母体为Ni3Al,并析出块状的富Re和W的化合物.