新设计了Ti-Zr-Cu-Ni-Co系钛基钎料,相对于B∏P16钎料,其Zr含量有所提高,而Cu,Ni,Co三种合金元素的总含量低于B∏P16钎料中Cu,Ni的总量.在960℃/10min的真空加热条件下,进行了两种钎料对TC4合金的熔化实验和连接实验.通过SEM和XEDS分析了接头组织和微区成分.钎焊接头力学性能试验结果表明,使用新钎料对应接头冲击韧性值为31.55J/cm3,比B∏P16钎料提高了56%,同时接头的剪切强度提高约20%.
参考文献
| [1] | BOTSTEIN O;RABINKIN A .Brazing of titanium-based alloys with amorphous 25wt% Ti-25wt% Zr-50wt% Cu filler metal[J].Materials Science and Engineering A,1994,188(1-2):305-315. |
| [2] | INOUE H;OGAWA T .Studying on welding of titanium alloys(Report 2)[J].Quarterly Journal of Japan Welding Society,1991,9(01):136-142. |
| [3] | STEFFENS H;DEGELMANN E .Simplified high-temperature brazing process for titanium and titanium alloys using an amorphous brazing filler metal[J].Schweissen and Schneiden,1990,42(05):70-71. |
| [4] | 郭万林 .钛基钎料的活性及理化性能对比研究[J].材料科学与工艺,1999,7(ZK):217-219. |
| [5] | Y LIJIMA O;HIRANO K .Reaction diffusion in the Cu-Ti system[J].Journal of the Japan Institute of Metals,1990,54(06):619-627. |
| [6] | ONZAWA T;SUZUMURA A;KO M W .Brazing of titanium using Low-melting-point Ti-based filler metals[J].Welding Journal,1990,69(12):462-467. |
| [7] | 李晓红.钛、锆及其合金的钎焊[A].北京:机械工业出版社,1998 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%