通过扫描电镜原位拉伸和原位疲劳实验,动态跟踪观察了SiO2类非金属夹杂物对FGH95合金裂纹萌生和扩展的影响规律.结果表明,在原位拉伸过程中,夹杂物处是裂纹萌生的择优位置,且沿与应力轴垂直或约45°向夹杂内部扩展.当主裂纹扩展到基体中之后,呈锯齿状向基体内扩展,但主裂纹所在平面仍与主应力轴垂直,其尖端变形带内有明显的滑移线出现.在原位疲劳过程中,主裂纹在夹杂物与基体界面处萌生,并在尖角应力集中处沿与主应力轴成45°向基体中扩展,随后沿垂直于主应力轴方向扩展至失稳断裂.夹杂物附近基体中的贫γ′相区,断口在两种加载条件下呈不同的断裂特征.
参考文献
| [1] | KISSINGER R D.[A].Warrendale,Penn,USA:TMS Society,1996:359. |
| [2] | SHAMBLEN C E;CHANG D R .Effect of inductions on LCF life of HIP plus heat treatment powder metal rene95[J].Metallurgical and Materials Transactions B:Process Metallurgy and Materials Processing Science,1985,16:775-784. |
| [3] | ANTOLOUICH S D.[A].Warrendale,Penn,USA:TMS Society,1992:13. |
| [4] | SIMS C T;STOLOFF N S;HAFEL W C.Superalloy,High Temperature Materials for Aerospace and Industrial Power[M].New York:John Wiley and Sons,Inc,1987:291. |
| [5] | CREMISIO R S;SIMS C T;HAGEL W C.The Superalloys[M].New York:Wilew,1972:373. |
| [6] | 李为镠.钢中非金属夹杂物[M].北京:冶金工业出版社,1998:461. |
| [7] | ZHOUXM;WANGWX;TANGDZ.Microstructure behavior study of non-metallic inclusions in HIPed P/M superalloy[A].Paris,France,2005:264-270. |
| [8] | 周晓明,汪武祥,杨洪涛,唐定中,颜鸣皋.HIP态FGH96合金中人工加入非金属夹杂物的特征[J].航空材料学报,2005(04):1-5. |
| [9] | 徐秉业;刘信声.应用弹塑性力学[M].北京:清华大学出版社,2003:1-3. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%