研究了Nb-Si-Ti-Hf-Cr-Al-B-Y合金在电子束区熔炉上的定向凝固组织、室温断裂韧性和高温瞬时拉伸性能.合金的组织主要由Nb基固溶体(Nbss)、α-(Nb)5Si3和(Nb)3Si相组成.定向凝固后,初生Nbss枝晶以及Nbss+α-(Nb)5Si3/(Nb)3Si层片状或棒状共晶团均沿着试棒轴线定向排列.当电子枪移动速率R=2.4 mm/min时,定向效果最好.定向凝固使合金在1250℃的拉伸强度及室温断裂韧性均显著提高.R=2.4 mm/min试棒的抗拉强度最高,达85.0 MPa,同时其室温断裂韧性也达到19.4 MPa·m1/2.
参考文献
| [1] | BEWLAYB P;JACKSONM R;ZHAO J-C et al.Areview of very-high-temperature Nb-silicide-based composites[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2003,34(10):2043-2052. |
| [2] | B.P. Bewlay;M.R. Jackson;J.-C. Zhao;P. R. Subramanian;M.G. Mendiratta;J.J. Lewandowski .Ultrahigh-Temperature Nb-Silicide-Based Composites[J].MRS bulletin,2003(9):646-653. |
| [3] | DIMIDUK D M;MIRACLE D B;WARD C H .Development of intermetallic materials for aerospace systems[J].Materials Science and Technology,1992,8(04):367-375. |
| [4] | Jiangbo Sha;Hisatoshi Hirai;Tatsuo Tabaru;Akira Kitahara;Hidetoshi Ueno;Shuji Hanada .High-temperature strength and room-temperature toughness of Nb-W-Si-B alloys prepared by arc-melting[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):151-158. |
| [5] | M.R.Jackson;B.P.Bewlay .High-Temperature Refractory Metal-Intermetallic Composites[J].JOM,1996(1):39-44. |
| [6] | CHANG K-M;BEWLAY B P;SUTLIFF J A.Coldcrucible directional solidification of refractory metal-silicide eutectics[J].Journal of The Minerals,Metals & Materials Society,1992:59-63. |
| [7] | BEWLAY B P;JACKSON M R;LIPSITT H A .The balance of mechanical and environmental properties of a multielement niobium-niobium silicide-based in situ composite[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1996,27(12):3801-3808. |
| [8] | D.VAN HEERDEN;A.J. GAVENS;P.R. SUBRAMANIAN .The Stability of Nb/Nb_5Si_3 Microlaminates at High Temperatures[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2001(9):2363-2371. |
| [9] | P.Guan,X.P.Guo,X.Ding,J.Zhang,L.M.Gao,K.Kusabiraki.DIRECTIONALLY SOLIDIFIED MICROSTRUCTURE OF AN ULTRA-HIGH TEMPERATURE Nb-Si-Ti-Hf-Cr-Al ALLOY[J].金属学报(英文版),2004(04):450-454. |
| [10] | X.P. Guo;P. Guan;X. Ding .Unidirectional Solidification of a Nb_(ss)/Nb_5Si_3 in-Situ Composite[J].Materials Science Forum,2005(Pt.1):745-748. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%