选择Al2O3(YAG)作为基体片层材料,LaPO4作为界面层材料,采用凝胶注模成型技术制备出基体层材料的坯片,然后在基体层坯片上采用浸渍或喷涂工艺附着界面层材料,最后将坯片叠置于模具中热压烧结.制备的陶瓷复合材料微观结构均匀,基体片层厚度为110-150μm,界面层厚度为10～30μm,实测层厚比为11.重点研究工艺参数及界面层成分对层状陶瓷复合材料室温性能的影响.结果表明,氧化物基层状陶瓷复合材料的抗弯强度比基体材料略有下降,但室温断裂韧性达到了13.52MPa·m1/2,是基体材料断裂韧性的3倍.对比氧化物基层状陶瓷复合材料与基体材料在断裂过程中裂纹扩展路径的差异.
参考文献
| [1] | LAWN BRIAN R;PADTURE NITIN P;CAI Hong-da et al.Making ceramics "Ductile"[J].Science,1994,263:1114-1116. |
| [2] | CLEGG W J;KENDALL K;ALFORD N M .A simple way to make tough ceramics[J].Nature,1990,347(10):455-447. |
| [3] | Liu HY.;Hsu SM. .FRACTURE BEHAVIOR OF MULTILAYER SILICON NITRIDE/BORON NITRIDE CERAMICS[J].Journal of the American Ceramic Society,1996(9):2452-2457. |
| [4] | Kovar D.;Halloran JW.;Thouless MD. .Crack deflection and propagation in layered silicon nitride boron nitride ceramics[J].Journal of the American Ceramic Society,1998(4):1004-1012. |
| [5] | YAROSHENKO V;ORLOVSKAYA N et al.Laminar Si3N4-TiN hot-prossed ceramic composites[J].Key Engineering Materials,1997,132-136:2017-2020. |
| [6] | MARSHALL D B;RATTO J J .Enhanced fracture toughness in layered microcomposites of Ce-ZrO2 and Al,O3[J].Journal of the American Ceramic Society,1991,74(12):2979-2987. |
| [7] | S.K.pateras;S.J.Howard;T.W.Clyne .The contribution of bridging ligament rupture to energy absorption during fracture of metal-ceramic laminates[J].Key engineering materials,1997(2):1127-1136. |
| [8] | Dov Sherman .The mechanical behavior of layered brazed metal/ceramic composites[J].Materials Letters,1998(56):255-260. |
| [9] | MC. Shaw .The Fracture Mode of Ceramic/Metal Multilayers: Role of the Interface[J].Key engineering materials,1996(116/117):261-278. |
| [10] | CAO H C;EVANS A G .On crack extension in ductile/brittle laminates[J].Acta Metallurgica Et Materialia,1991,39(12):2997-3005. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%