利用SEM,XRD和EPMA详细分析K4104镍基高温合金料浆渗Al-Si的微观结构.结果表明,表层主要为富Al的β-NiAl+CrxSiy化合物,过渡层主要为富Ni的β-NiAl相,内扩散层主要为β-NiAl相+富Cr相+γ'-Ni3Al相+Ni固溶体.