分别采用E20和E51环氧树脂与双酚A型二氰酸酯(BADCy)共聚来改善氰酸酯树脂的力学性能.用DSC,FTIR研究了两种不同分子量的环氧改性氰酸酯体系的反应性,发现E20和E51对BADCy的固化反应均有催化作用,但E20的催化作用强于E51.断面SEM表明,经E20和E51改性的BADCy断口处存在大量的韧涡.但改性体系的热变形温度(HDT)和吸水率有所下降,当配比(质量)相同时,E51/BADCy体系比E20/BADCy体系具有更高的HDT和较小的吸水率.
参考文献
| [1] | HAMERTON Ian;HAY John N .Recent developments in the chemistry of cyanate esters[J].Polymer International,1998,47(04):465-473. |
| [2] | P.Bartolomeo;J.F.Chailan;J.L.Vernet .Curing of cyanate ester resin: a novel approach based on FTIR spectroscopy and comparison with other techniques[J].European Polymer Journal,2001(4):659-670. |
| [3] | CHAPLIN Adam;HAMERTON Ian;HOWLIN Brendan J et al.Development of Novel Functionalized Aryl Cyanate Ester Oligomers.1.Synthesis and Thermal Characterization of the Monomers[J].Macromolecules,1994,27:4927-4935. |
| [4] | Chaplin A. .Studying water uptake effects in resins based on cyanate ester/bismaleimide blends[J].Polymer: The International Journal for the Science and Technology of Polymers,2000(11):3945-3956. |
| [5] | KASEHAGEN Leo J;MACOSKO Christopher W .Structure Development in Cyanate Eater Polymerization[J].Polymer International,1997,44:237-247. |
| [6] | Srinivasan SA.;McGrath JE. .Amorphous phenolphthalein-based poly(arylene ether) modified cyanate ester networks: 1. Effect of molecular weight and backbone chemistry on morphology and toughenability[J].Polymer: The International Journal for the Science and Technology of Polymers,1998(12):2415-2427. |
| [7] | Srinivasan SA.;Kranbeuhl D.;Ward TC.;Mcgrath JE.;Joardar SS. .AMORPHOUS PHENOLPHTHALEIN-BASED POLY(ARYLENE ETHER)-MODIFIED CYANATE ESTER NETWORKS - MICROWAVE PROCESSING[J].Journal of Applied Polymer Science,1997(1):179-190. |
| [8] | Sunil K. Karad;Frank R. Jones;David Attwood .Moisture absorption by cyanate ester modified epoxy resin matrices. Part II. The reverse thermal effect[J].Polymer: The International Journal for the Science and Technology of Polymers,2002(21):5643-5649. |
| [9] | Liang GZ.;Zhang MX. .Enhancement of processability of cyanate ester resin via copolymerization with epoxy resin[J].Journal of Applied Polymer Science,2002(11):2377-2381. |
| [10] | Mathew Dona;Ninan K.N.;Reghunadhan Nair C.P. .Bisphenol A dicyanate-novolac epoxy blend: cure characteristics, physical and mechanical properties, and application in composites[J].Journal of Applied Polymer Science,1999(7):1675-1685. |
| [11] | Borrajo J.;Williams RJJ.;Cao ZQ.;Pascault JP.;Riccardi CC. .RUBBER-MODIFIED CYANATE ESTERS - THERMODYNAMIC ANALYSIS OF PHASE SEPARATION[J].Polymer: The International Journal for the Science and Technology of Polymers,1995(18):3541-3547. |
| [12] | FANG T;SHIMPD A .Polycyanateesters:Science and applications[J].Progress in Polymer Science,1995,20:61-118. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%