采用SEM和XRD分析热处理后合金试样的显微组织及相组成,用TEM分析原始组织中钇的存在方式.结果表明,钇在原始组织中以Y2O3形式存在;钇增加O相衍射峰,提高Ti-23Al-25Nb合金压缩性能,如抗压强度、压缩率等,钇的强化作用是由于Y2O3第二相粒子强化和钇细化晶粒的晶界强化共同作用的结果.
参考文献
| [1] | GOGIA A K;NANDY T K;BANERJEE D et al.Microstructure and mechanical properties of orthorhombic alloys in the Ti-Al-Nb system[J].Intermetallics,1998,6(7-8):741-748. |
| [2] | CHU F;MITCHELL T E;MAJUMDAR B et al.Elastic properties of the O phase in Ti-Al-Nb alloys[J].Intermetallics,1997,5(02):147-156. |
| [3] | REN X;HAGIWARA M.Displacive precursor phenomena in Ti-22Al-27Nb intermetallic compound to diffusional transformation[J].Acta Materialia,2001(49):3971-3980. |
| [4] | FENG T;NAKAZAWA S;HAGIWARA M .Creep behavior of tungsten-modified orthorhombic Ti-22Al-22Nb-2W alloy[J].Scripta Materialia,2000,43:1065-1070. |
| [5] | C. J. Boehlert .The effects of forging and rolling on microstructure in O + BCC Ti-Al-Nb alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):118-129. |
| [6] | 吴波,沈剑韵,张翥,孙军,彭德林,柳松青.Ti2AlNb基合金的计算机模拟研究进展[J].稀有金属材料与工程,2002(04):241-245. |
| [7] | 毛勇,李世琼,张建伟,彭继华,邹敦叙,仲增墉.Ti-22Al-20Nb-7Ta合金的显微组织和力学性能研究[J].金属学报,2000(02):135-140. |
| [8] | EMURA S;ARAOKA A;HAGIWARA M.B2 Grain size refinement of (O+B2) Ti-22Al-27Nb Alloy[A].,2004:2153-2159. |
| [9] | 杜挺 .稀土元素在金属材料中的一些物理化学[J].金属学报,1997,33(01):69-77. |
| [10] | 张永刚;韩雅芳;陈国良.金属间化合物结构材料[M].北京:国防工业出版社,2001:789-797. |
| [11] | GERMANN L;BANERJEE D;GUEDOU J Y.Microstructure-property relationships in newly developed multiphase Ti2AlNb-based titanium aluminides[A].,2004:2137-2144. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%