利用薄壁管拉扭疲劳试样, 在高温控制应变循环加载下研究高温合金GH4169的多轴疲劳行为.高温多轴疲劳试验采用比例与非比例加载路径.在试验过程中,利用数据采集系统全程记录拉与扭的应力响应值以研究比例与非比例拉扭加载下的循环特性.研究结果表明,高温拉扭非比例加载下,疲劳寿命有明显降低;拉与扭应力响应多为循环软化,无明显的循环稳定现象.在低频加载下,由于高温蠕变效应加大,使循环软化速度加快,表现为曲线下降明显.在整个疲劳过程中,扭转应力响应分量均显示循环软化现象,而拉压应力响应分量的硬化与软化特性取决于应变加载参数.
参考文献
| [1] | TATSUO INOUE;SHIGERU KISHI;HIROYUKI KOTO et al.Fatigue-creep life prediction of 2(1)/(4) Cr-1Mo steel under combined tension-torsion at 600℃[J].Nuclear Engineering and Design,1994,150:119-127. |
| [2] | TATSUO INOUE;FUSAHITO YOSHIDA;YASUSHI NIITSU et al.Inelastic stress-strain response of Cr-1Mo steel under combined tension-torsion at 600oC[J].Nuclear Engineering and Design,1994,150:107-118. |
| [3] | TATSUO INOUE;MASAKAZU OKZAZKI;TOSHIHIDE IGARI et al.Evaluation of fatigue life prediction methods in multiaxial stress state[J].Nuclear Engineering and Design,1991,126:13-21. |
| [4] | ASADA Y;ASAYAME T;MORIISHITA M.Creep-fatigue damage evaluation of 304 stainless steel and 2.25Cr-1Mo steel based on the overstress concept[A].ASME,PVP,1988:93-99. |
| [5] | NAKAMURA T;ISHIKAWA T;ASADA Y .Relaxation behavior of 304 stainless steel under tension-torsion biaxial loading[J].International Journal of Pressure Vessels and Piping,1992,51:211-227. |
| [6] | Lianqing Wang,Jianguo WANG,Hongying Wang,Shiping Xu,Deguang Shang.Interaction of fatigue and creep of GH33 under multi-axial stress at high temperature[J].北京科技大学学报(英文版),2003(02):80-80. |
| [7] | HUANG Si-jing;TANG Jun-wu;WANG Jian-guo.Life prediction under multiaxial stresses with creep-fatigue interaction[A].,1996:64. |
| [8] | 陈立佳.镍基高温合金的蠕变-疲劳交互作用行为及寿命预测[J].航空材料学报,1998(03):1. |
| [9] | TATSUO INOUE;MASAKAZU OKZAZKI;TOSHIHIDE IGARI et al.Evaluation of fatigue life prediction methods in multiaxial stress state[J].Nuclear Engineering and Design,1991,126:13-21. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%