研究了热处理对铸态高Nb-TiAl合金组织中S-偏析的影响.试验结果表明,对合金试样在Tα温度以上(1350～1400℃)进行热处理可以消除S-偏析,短时间内保温组织中会再次出现大量的β相,长时间保温后β相完全溶解并转变为α相,其冷却到室温变为片层组织;在Tα温度以下α+γ两相区(1250～1330℃)由于γ相的存在不能消除S-偏析.合金试样经过1350℃/24h+900℃/30min/AC和1400℃/12h+900℃/30min/AC处理后,S-偏析都得到了有效的消除,并分别获得平均晶粒尺寸为210μm和 120μm的片层组织.
参考文献
| [1] | XJ. Xu;J.P. Lin;Z.K. Teng .On the microsegregation of Ti-45Al-(8-9)Nb-(W, B, Y) alloy[J].Materials Letters,2007(2):369-373. |
| [2] | Z.W. HUANG .Inhomogeneous microstructure in highly alloyed cast TiAl-based alloys, caused by microsegregation[J].Scripta materialia,2005(10):1021-1025. |
| [3] | BROSSMANN U;OEHRING M;APPEL F.Microstructure and chemical homogeneity of high Nb gamma based TiAl alloys in different conditions of processing[A].TMS:Warrendale:PA,2001:191-200. |
| [4] | 高建峰,徐向俊,林均品,宋西平,王艳丽,林志,陈国良,李树索,苏喜孔,韩雅芳.热变形高铌TiAl合金室温塑性研究[J].稀有金属材料与工程,2005(09):1497-1499. |
| [5] | DUARTE A;VIANA F;HENRIQUE M;CANTOS C M .As-cast titanium aluminides microstructure modification[J].Material Research,1992,2(03):191-195. |
| [6] | SEMINATIN S L;NEKKANTI R;ALAM M K et al.Homogenization of near-gamma titanium aluminides:analysis of kinetics and process scaleup feasibility[J].Metallurgical Transactions,1993,24:1259-1306. |
| [7] | CHEN G L;ZHANG W J;LIU Z C.Microstructure and properties of high Nb containing TiAl alloys[A].TMS:Warrendale:PA,1997:371-380. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%