通过将5Al-Ti体系混合粉末预制块在一定温度下预热,原位制备出Al3Ti/Al复合材料,并探讨了其生成机理和影响因素.研究发现:Al粉和Ti粉混合预热生成Al3Ti是由Al粉的熔化诱导;在高于热爆起始温度下预热时,Al3Ti直接以热爆反应机制生成;在低于热爆起始温度下预热时,Al3Ti按扩散-热爆反应机制生成.预热温度、Ti粉粒度及冷却速度是影响材料组织性能的关键因素.通过适当工艺制备出具有性能优异的Al3Ti/Al复合材料,其硬度是铝基体的3.6倍,耐磨性高.
参考文献
| [1] | MUOZ-MORRIS M A;REXACH J I;Lieblich M .Comparative study of Al-TiAl volume fractions and particle sizes[J].Intermetallics,2005,13:141-149. |
| [2] | Jung-Moo Lee;Suk-Bong Kang;Tatsuo Sato .Fabrication of Al/Al_3Fe composites by plasma synthesis method[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):199-209. |
| [3] | ROBERTM H;URTIGA FILHO S L .Mechanical properties of Al-NbAl3 in-situ composites[J].Journal of Materials Processing Technology,1997,64:335-341. |
| [4] | VELASCO F;LIMA W M;ANT N N .Effect of intermetallic particles on wear behaviour of stainless steel matrix composites[J].Tribology,2003,36:547-551. |
| [5] | 严有为,傅爱琼,魏伯康,林汉同.基于SHS技术制备Al-Ti-C晶粒细化剂的研究[J].铸造,2004(12):980-983. |
| [6] | 介万奇,E.G.Kandalova,张瑞杰,V.I.Nikitin.SHS法制备Al3Ti/Al复合材料的研究[J].稀有金属材料与工程,2000(03):145-148. |
| [7] | 朱和国,王恒志,吴申庆.α-Al2O3,TiB2颗粒增强铝基复合材料的XD合成[J].金属学报,2001(03):321-324. |
| [8] | 梁英教;车荫昌.无机物热力学数据手册[M].沈阳:东北大学出版社,1994:383. |
| [9] | 叶大伦.实用无机物热力学数据手册[M].北京:冶金工业出版社,1981:57,1061. |
| [10] | 吴引江,兰涛.漫渗燃烧合成TiAl金属间化合物的物化过程探讨[J].稀有金属材料与工程,1996(02):17-20. |
| [11] | 张俊善,汪涛,祝美丽,刘瑞岩.燃烧合成TiAl3化学反应动力学研究[J].金属学报,2002(10):1027-1030. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%