利用热重分析法(TG)和扫描电子显微镜(SEM)研究了微量元素P对Thermo-Span合金650℃氧化行为的影响.结果表明,氧化增重遵循抛物线规律,氧化层分两部分,包括氧化外层和氧化过渡层.外层富Fe,Co,O元素,氧化过渡层富Nb,Al,Cr,O等元素,Fe,Co,O含量降低.0.001%磷合金表层氧化物主要为针状的Fe,Co氧化物,而0.023%磷含量合金表层氧化物则大部分为块状Co的氧化物,随磷含量增加,表层Fe元素含量降低.0.023%磷阻碍Fe元素向外迁移及氧的向内扩散,降低合金在650℃下的氧化速率,提高合金650℃的抗氧化性能.
参考文献
| [1] | GUO S R;SUN W;LU D.Effect of minor elements on microstructure and mechanical properties of IN718 alloy[A].Warrendale,PA:TMS-AIME,1997:521-530. |
| [2] | SUN W;GUO S R;LU D Z et al.Effect of phosphorus on the microstructure and stress rupture properties in an Fe-NiCr base superalloy[J].Metallurgical and Materials Transactions A,1997,28:649-654. |
| [3] | SUN W;GUO S R;HU Z Q et al.Effect of phosphorus on the δ-Ni3 Nb phase precipitation and stress rupture properties in alloy 718[J].Materials Science and Engineering,1998,A247:173-179. |
| [4] | Zhu L Y.A new way to improve superalloys[A].Warrendale,PA:TMS-AIME,1992:145-154. |
| [5] | Song H;Hu Z;Guo S .Beneficial effect of phosphorus on the creep behavior of Inconel 718[J].Scripta materialia,1999(2):215-219. |
| [6] | 宋洪伟 .磷对IN718合金组织演化和力学性能的影响[D].中国科学院金属研究所,1999. |
| [7] | 孙文儒 .微量元素P,S和Si和Si对In718和GH761合金凝固过程,元素偏析, 组织结构和力学性能的影响[D].中国科学院金属研究所,1996. |
| [8] | BRAINT C L .Grain boundary segregation in the Ni-base alloy 182[J].Surface and Interface Analysis,1990,16:552-558. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%