研究了不同粒径SiC对氟醚硫化胶力学性能,导热性能和摩擦磨损性能的影响.结果表明,随着SiC粒径的减小,橡胶100%定伸模量增大,拉伸强度提高;填充体积含量为15%的20nm SiC时橡胶的综合力学性能比较优异;大粒径SiC与基体间的界面热阻更小,比小粒径填料更能提高橡胶的导热性能;不同粒径的SiC以一定比例并用也可以提高橡胶的导热系数;SiC晶须能显著提高橡胶的摩擦磨损性能.
参考文献
| [1] | 栗付平;边俊峰;张洪雁 .耐低温氟醚橡胶补强体系的研究[J].特种橡胶制品,1998,19(01):11-13. |
| [2] | Geon-Woong Lee;Min Park;Junkyung Kim .Enhanced thermal conductivity of polymer composites filled with hybrid filler[J].Composites, Part A. Applied science and manufacturing,2006(5):727-734. |
| [3] | TAVMAN I H .Effective thermal conductivity of isotropie polymer composites[J].International Journal of Heat Mass and Transfer,1998,25(05):723-732. |
| [4] | Qun-Ji Xue;Qi-Hua Wang .Wear mechanisms of polyetheretherketone composites filled with various kinds of SiC[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1997(1/2):54-58. |
| [5] | ZHANG Z;BREIDT C;CHANG L et al.Enhancement of the wear resistance of epoxy:shout carbon fiber,graphite,PTFE and nano-TiO2[J].Composites (A),2004,35:1385-1392. |
| [6] | Ishida H.;Rimdusit S. .Very high thermal conductivity obtained by boron nitride-filled polybenzoxazine[J].Thermochimica Acta: An International Journal Concerned with the Broader Aspects of Thermochemistry and Its Applications to Chemical Problems,1998(1/2):177-186. |
| [7] | Yang J;Tian M;Jia QX;Zhang LQ;Li XL .Influence of graphite particle size and shape on the properties of NBR[J].Journal of Applied Polymer Science,2006(4):4007-4015. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%