针对SiCf/β21S钛基复合材料,采用Ti-Zr-Cu-Ni-Co系新钎料,进行了钎焊实验和接头力学性能测试.实验结果表明:960℃/10min规范下的钎缝组织形貌单一,钎焊接头剪切强度平均值为157.8MPa;960℃/10min/5MPa规范下的钎缝主要由层片状组织组成,接头剪切强度平均值达到291.2MPa,较前者提高了85%左右,该接头经过900℃/2h热处理后组织变化不大.钎缝中的缺陷以及Ti和Zr与Cu,Ni和Co三种合金元素形成的脆性化合物相在接头中所占比例对接头性能影响很大.
参考文献
| [1] | 张启运;庄鸿寿.钎焊手册[M].北京:机械工业出版社,1998 |
| [2] | Yang YQ.;Kumpfert J.;Dudek HJ. .Interfacial reaction and stability of SCS-6 SiC/Ti-25Al-10NB-3V-1MO composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):213-220. |
| [3] | CHANG D J;KAO W H .SiC reinforced titanium corrugated structures for high temp.application[J].SAMPI Journal,1998,24(02):336-340. |
| [4] | UPADHYAYA D;AANDHU S .Interfacial reactions in Ti-6Al-4V/σ-1240 fibre metal matrix composite[J].Materials Science and Technology(A),1995,11:1156-1161. |
| [5] | MOGILEVSKY P .Application of diffusion barriers in composite materials[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1998,242:235-247. |
| [6] | SUBRRAMANIAN P R .Fabrication of SiC fibre reinforced titanium matrix composite by magnetron sputtering[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1998,244:1-5. |
| [7] | 吕祥鸿,杨延清.Ti基复合材料界面反应扩散的微观分析[J].材料工程,2008(06):21-24,28. |
| [8] | 陈波,毛唯,谢永慧,熊华平,程耀永,郭万林,李晓红.Ti-Zr-Cu-Ni-Co系新钎料的成分设计及TC4合金钎焊接头的力学性能[J].航空材料学报,2006(01):59-62. |
| [9] | 虞觉奇;易文质;陈邦迪.二元合金状态图集[M].上海:上海科学技术出版社 |
| [10] | 郭万林,李天文.钛合金钎缝中元素的扩散行为研究[J].稀有金属,2001(05):345-348. |
| [11] | 吴铭方,蒋成禹,于治水,梁超.TC4/72Ag-28Cu 钎焊组织及Ti-Cu化合物[J].航空材料学报,2001(03):29-32. |
| [12] | 蒋成禹,吴铭方,余春,梁超.72Ag-28Cu钎焊TC4的接头组织及强度[J].稀有金属材料与工程,2003(04):295-297. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%