采用亚快速定向凝固装置成功地制备了Ti-47.5Al-2Cr-2Nb-0.2B合金定向凝固试样,观察了不同凝固速率下的固液界面形貌、过渡区和稳态区凝固组织.实验结果表明,在2μm/s抽拉速率下,合金界面以胞状界面形态生长,全片层组织(γ+α2)取向与生长方向成0°和45°的夹角,合金凝固时的领先相为β相.在100μm/s凝固速率下,合金界面以枝状形态生长,全片层组织方向与生长方向的夹角为90°,领先相从β相转化为α相.通过将合金中Cr和Nb元素的含量折算成Al的含量,计算Ti-48.3Al合金中α和β相界面生长温度,发现凝固速率达到180μm/s时,领先相可由β相转变为α相,理论计算结果支持实验中的相选择转变过程.
参考文献
| [1] | 李成功;傅恒志;于翘.航空航天材料[M].北京:国防工业出版社,2001:103. |
| [2] | J.Yamaguchi;H.Inui .High-temperature structural intermetallics[J].Acta materialia,2000(1):307-322. |
| [3] | YAMAGUCHI M;INUI H.[A].Warrendale:TMS,1993:127. |
| [4] | KIM Y W;DIMIDUK D M et al.Processing ECETS 2000-ISAM[D].北京,2000. |
| [5] | Dimiduk DM .Gamma titanium aluminide alloys--an assessment within the competition of aerospace structural materials[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(2):281-288. |
| [6] | INUI H;NAKAMURA A;YAMAGUCHI M .Room-temperature tensile deformation of polysynthetically twinned crystals of TiAl[J].Acta Metallurgica Et Materialia,1992,40(07):3059-3104. |
| [7] | 张永刚;韩雅芳;陈国良.金属间化合物结构材料[M].北京:国防工业出版社,2001:736-738. |
| [8] | M.Yamaguchi;D.R.Johnson .Directional solidification of TiAl-base alloys[J].Intermetallics,2000(5/6):511-517. |
| [9] | JOHNSON D R;MASUDA Y;INUI H.Alignment of the TiAl/Ti3 Al lamellar microstructure in TiAl alloys by directional solidification[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1997(239-240):577-583. |
| [10] | YAMANAKA T;JOHNSON D R;INUI H et al.Directional solidification of TiAl-Re-Si alloys with aligned lamellar microstructures[J].Intermetallics,1997,7:779-784. |
| [11] | 傅恒志,郭景杰,苏彦庆,刘林,徐达鸣,李金山.TiAl金属间化合物的定向凝固和晶向控制[J].中国有色金属学报,2003(04):797-810. |
| [12] | JOHNSON D R;INUI H;SH INJI Muto et al.Microstructural development during directional solidification of α-seeded TiAl alloys[J].Acta Materialia,2006,54:1084. |
| [13] | UMEDA T;OKANE T;KURZ W .Pase Selection during solidification of peritectic alloys[J].Acta Materialia,1996,40:4209-4216. |
| [14] | 钟宏,李双明,吕海燕,刘林,邹光荣,傅恒志.Nd-Fe-B 包晶合金的定向凝固组织及相选择[J].中国科学G辑,2007(03):303-312. |
| [15] | JOHNSON D R;INUI H;YAMAGUCHI M .Crystal growth of TiAl alloys[J].Intermetallics,1998,6:651. |
| [16] | SU Yan-qing;LIU Chang;LI Xin-zhong .Microstructure selection during the directionally peritectic solidification of Ti-Al binary system[J].Intermetallics,2005,13:271. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%