针对不同编织角、不同纤维体积含量、不同编织结构的三维编织T300/环氧复合材料进行了三点弯曲试验,获得了这些编织复合材料的主要弯曲力学性能,分析了不同编织工艺参数对材料弯曲力学性能的影响.对试件断口进行了宏观及扫描电镜观察,从宏、细观角度研究了材料的变形及其破坏机理.结果表明,三维编织T300/环氧复合材料具有良好的弯曲力学性能,弯曲载荷-挠度曲线呈现明显的线性特征;编织角、纤维体积含量及编织结构对复合材料的弯曲性能有较大影响;三维编织复合材料的弯曲破坏机理与编织工艺参数有关.
参考文献
| [1] | YAU S S;CHOU T W;KO F K .Flaexural and axial compressive failures of three-dimensionally braided composite I -beam[J].COMPOSITES,1986,17(03):490-512. |
| [2] | SHIVAKUMAR K N;EMEHEL T C;AVVA V S et al.Compression strength and failure mechanism s of 3-D textile composites.[AIAA -95-1159][R].New York:AIAA,1995. |
| [3] | Li, DS;Lu, ZX;Chen, L;Li, JL .Microstructure and mechanical properties of three-dimensional five-directional braided composites[J].International Journal of Solids and Structures,2009(18/19):3422-3432. |
| [4] | LID S;LU Z X;FANG D N.Longitudinal compressive behavior and failure mechanism of three-dimensional fivedireectional carbon/phenolic braided composites at high strain rates[J].Materials Science and Engineering (A),2009 |
| [5] | 刘谦,李嘉禄,李学明.三维编织工艺参数对复合材料拉伸性能的影响[J].宇航材料工艺,2000(01):55-58. |
| [6] | 陈利,梁子青,马振杰,刘景艳,李嘉禄.三维五向编织复合材料纵向性能的实验研究[J].材料工程,2005(08):3-6. |
| [7] | 李仲平,卢子兴,冯志海,李典森.三维五向碳/酚醛编织复合材料的拉伸性能及破坏机理[J].航空学报,2007(04):869-873. |
| [8] | 李典森,刘子仙,卢子兴,冯志海.三维五向炭纤维/酚醛编织复合材料的压缩性能及破坏机制[J].复合材料学报,2008(01):133-139. |
| [9] | LI J L;JIAO Y N;SUN Y et al.Experimental investigation of cut-edge effect on mechanical properties of three-dimensional braided composites[J].Materials & Design,2007,28(01):2417-2424. |
| [10] | 卢子兴,刘振国,寇长河,麦汉超,唐国翌,冯志海.三维编织复合材料的弯曲实验及其失效分析[C].复合材料—生命、环境与高技术（第12届全国复合材料学术会议：论文专辑）,2002:1070-1073. |
| [11] | 王波,矫桂琼,陶亮,耿小亮.三维编织T300/QY9512弯曲性能的实验研究[J].西北工业大学学报,2003(05):552-555. |
| [12] | 李嘉禄,魏丽梅,杨红娜.碳纤维三维编织复合材料的结构对拉伸和弯曲性能的影响[J].材料工程,2004(12):3-7. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%