对YB-DM-11航空有机玻璃试样在254nm和313nm两种波长的紫外光照射下,进行了2个月的加速老化试验,跟踪测试了有机玻璃的抗拉强度和重量变化规律.通过红外光谱(FTIR)、热分析(TG/DTA)、扫描电镜(SEM)和凝胶渗透色谱(GPC)等方法,分析了老化前后试样的结构和性能,结合老化前后有机玻璃的性能变化规律,揭示了有机玻璃在紫外光照射下的老化机理.
The accelerated ageing experiment of Perspex (PMMA) YB-DM-11 were done for nearly two months in both 254nm and 313nm wave length ultraviolet. Tensile stress and mass were measured during the experiment. Thus the changing rules of both parameters were obtained. The samples structure difference were founded between before ageing and after ageing by methods of IR, TG/DTA,GPC and SEM. Analyzed results above all, the ageing mechanisms of PMMA in ultraviolet were clarified qualitatively.
参考文献
| [1] | 化学工业部合成材料研究所.高分子材料老化与防老化[M].北京:化学工业出版社,1979:38-61. |
| [2] | 李善君;纪桂.高分子光化学原理及应用[M].上海:复旦大学出版社,1993:264-267. |
| [3] | 沈莉莉;马丽婷;陈新文 .YB-DM-3航空有机玻璃的热老化性能[J].中国有色金属学报,2005,15(z2):2100-2104. |
| [4] | 马丽婷;陈新文;苏彬 .有机玻璃在湿热条件下的老化机理[J].中国有色金属学报,2005,15(02):441. |
| [5] | 马丽婷,陈新文,苏彬.有机玻璃在盐水条件下老化性能的研究[J].塑料工业,2007(07):58-60. |
| [6] | 马丽婷;陈新文;苏彬 .有机玻璃在自来水条件下力学性能的研究[J].实验室研究与探索,2007,26(11):166. |
| [7] | 黄宝臣.航空有机玻璃紫外线加速老化方法初探[J].飞机设计,1995(01):46-52. |
| [8] | 马占镖.甲基丙烯酸酯树脂及其应用[M].北京:化学工业出版社,2001:278. |
| [9] | 谢缅诺维奇Г M;赫拉莫娃 T C.聚合物物理化学手册:聚合物的红外光谱和核磁共振谱[M].北京:中国石化出版社,1995:142-149. |
| [10] | 夏笃祎;张肇熙.高聚物结构分析[M].北京:化学工业出版社,1990:49-66. |
| [11] | 刘凤岐;汤心颐.高分子物理[M].北京:高等教育出版社,1995:350-398. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%