自行设计开发了适合工业化生产高纯净,低偏析,无宏观缺陷铸锭的电渣重熔连续定向凝固技术(ESR-CDS)的设备和工艺,利用该技术成功制备了直径为φ150mm的René88DT合金定向凝周铸锭.采用XRD测试了定向凝固柱状晶的生长取向,结果表明,ESR-CDS René88DT铸锭柱状晶择优生长方向为<100>系晶向;ERS-CDS铸锭与传统ESR铸锭相比,枝晶组织生长方向保持一致,二次枝晶臂均匀细小,元素偏析程度低,且晶间一次析出相呈颗粒状,尺寸细小;等温热压缩实验结果表明,ESR-CDS René88DT合金热压缩试样在1100℃,0.0-50.1s-1应变速率下可达到70%以上压缩变形量并获得均匀细小的动态再结晶组织;ESR-CDS René88DT合金铸锭经等温锻造制备出了φ170mm×73mm的饼坯件,锻压变形量超过70%,饼坯件除上下两端的变形死区外均发生了动态再结晶,晶粒尺寸约50μm.
参考文献
| [1] | REED Roger C.The superalloys fundamentals and applications[M].Cambridge:Cambridge University Press,2006:229. |
| [2] | D. Ma;U. Grafe .Microsegregation in directionally solidified dendritic-cellular structure of superalloy CMSX-4[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(2):339-342. |
| [3] | 朱耀宵 .低偏析高温合金[J].金属热处理学报,1997,18(03):16-22. |
| [4] | Y.Z. Zhou;A. Volek .Effect of dendrite arm spacing on castability of a directionally solidified nickel alloy[J].Scripta materialia,2007(6):537-540. |
| [5] | Zhengdong Long;Xingbo Liu;Wanhong Yang;Keh-Minn Chang;Ever Barbero .Thermodynamic assessment of liquid composition change during solidification and its effect on freckle formation in superalloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):254-261. |
| [6] | M. A. Dunlavy;R. Shivpuri;S. L. Semiatin .Failure during hot working of spray-formed Rene' 88[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):210-219. |
| [7] | MEDOVAR L B;TSYKULENKO A K;SAENKO V Ya.NEW Electroslag Technologies[A].,2000:49-60. |
| [8] | 刘建涛,张义文,陶宇,刘国权,胡本芙.FGH96合金动态再结晶行为的研究[J].材料热处理学报,2006(05):46-50. |
| [9] | DAVIDE Alghisi;MICHELE Milano;LAURA Pazienza.The electroslag rapid remelting process under protective atmosphere of 145 mm billets[A].,2000:97-112. |
| [10] | 赵美兰,孙文儒,杨树林,祁峰,郭守仁,胡壮麒.GH761变形高温合金的热变形行为[J].金属学报,2009(01):79-83. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%