利用Hopkinson压杆对Mg-3Li和Mg-3Li-1Sc合金进行了高应变率冲击实验,分析了添加少量Sc对Mg-3Li合金冲击变形行为及其应变率效应的影响.结果表明,在1350s～3000s-1应变率范围内,两种合金的动态应力-应变行为均表现出显著的应变率强化效应.但随应变率继续升高,合金的动态变形行为转为应变率弱化效应.在1350～3500s-1应变率下,Mg-3Li-1Sc合金比Mg-3Li合金的动态屈服强度显著提高.在高应变率冲击条件下,晶内滑移和孪生产生的加工硬化及微裂纹的产生、扩展致使二种合金的动态变形行为先呈现应变率强化效应而后呈现为应变率弱化效应.添加少量Sc后Mg-3Li合金显微组织的细化和细小弥散MgSc相的形成,是显著提高Mg-3Li-1Sc合金冲击变形抗力的主要原因.
参考文献
| [1] | DUAN C Z;WANG M;DOU T .Microscopic Examination of Primary Shear Zone in High Speed Machining of Hardened High Strength Steel[J].Journal of Manufacturing Science and Engineering,2010,97-101:1887-1890. |
| [2] | Yang, HJ;Xu, YB;Seki, Y;Nesterenko, VF;Meyers, MA .Analysis and characterization by electron backscatter diffraction of microstructural evolution in the adiabatic shear bands in Fe-Cr-Ni alloys[J].Journal of Materials Research,2009(8):2617-2627. |
| [3] | M. A. Meyers;Y. B. Xu;Q. Xue .Microstructural evolution in adiabatic shear localization in stainless steel[J].Acta materialia,2003(5):1307-1325. |
| [4] | LI Q;XU Y B .Dynamic Mechanical Behavior of Pure Titanium[J].Journal of Materials Processing Technology,2005,156:1889-1892. |
| [5] | XU Y-B;BAI Y L;MEYERS M A .Deformation,Phase Transformation and Recrystallization Induced during HighStrain Rate Loading in Shear Bands of Ti-6Al-4V Alloy[J].Materials Science and Technology,2006,22:737-7461. |
| [6] | Y. B. Xu;W. L. Zhong;Y. J. Chen;L. T. Shen;Q. Liu;Y. L. Bai .Shear localization and recrystallization in dynamic deformation of 8090 Al-Li alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1/2):287-295. |
| [7] | 毛萍莉,刘正,王长义,金鑫,王峰,郭全英,孙晶.高应变速率下AZ31B镁合金的压缩变形组织[J].中国有色金属学报,2009(05):816-820. |
| [8] | XU Y B;BAI Y L .Evolution of Thermoplastic Shear Localization and Related Microstructures in Al/SiCp Composites under Dynamic Compression[J].Journal of Materials Science and Technology,2002,19:504-508. |
| [9] | E. El-Magd;M. Abouridouane .Characterization, modelling and simulation of deformation and fracture behaviour of the light-weight wrought alloys under high strain rate loading[J].International journal of impact engineering,2006(5):741-758. |
| [10] | 胡昌明,李英雷,胡时胜,刘仓理.高温-高应变率下MB2合金的动态力学性能及变形机理[J].兵器材料科学与工程,2009(05):8-11. |
| [11] | 吴秀玲,谭成文.冲击载荷作用下AZ31镁合金中的变形局域化[J].稀有金属材料与工程,2008(06):1111-1113. |
| [12] | 沙桂英,刘翠云,刘腾,孙晓光,李根.添加Y对Mg-3.5%Li合金冲击变形行为的影响[J].材料工程,2010(07):64-67. |
| [13] | 孙晓光,沙桂英,刘腾,于涛,刘占英.添加微量Sc对Mg-3%Li合金组织与性能的影响[J].金属热处理,2010(03):29-32. |
| [14] | 陈振华.变形镁合金[M].北京:化学工业出版社,2005:331-334. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%