测定了定向有机玻璃YB-DM-11在应力比R＝-0.4,0.1和0.4下的中部区和加速扩展区的裂纹扩展速率.将适用于金属材料的双参量裂纹扩展驱动力模型K*＝(Kmax)a(△K+)1-a引入到有机玻璃裂纹扩展行为研究.对于有机玻璃,双参量裂纹扩展驱动力模型中的相关参数α并非定值,是与应力比、断裂韧度、应力场强度因子和裂纹扩展速率趋于无穷大时双参量动力模型中相关参数αb有关的函数.在一定应力比范围内,得到基于双参量动力模型的疲劳裂纹扩展速率通用表达式,能很好地表征不同应力比下的疲劳裂纹扩展行为,表明了应力比对有机玻璃疲劳裂纹扩展速率中部区和加速区的影响.
参考文献
| [1] | ELBER W.The significance of fatigue crack closure[A].Philadelphia (PA):American Society for Testing and Materials,1971:230-242. |
| [2] | MACHA D E;CORBLY D M;JONES J W .On the variation of fatigue crack opening loading with measurement location[J].Experimental Mechanics,1979,19:207-213. |
| [3] | SHIN C S;SMITH R A .Fatigue crack growth from sharp notches[J].International Journal of Fatigue,1985,7:87-93. |
| [4] | SAGANANDA K;VASUDEVAN A K.Analysis of fatigue crack closure and threshold[A].Philadelphia:American Society for Testing and Materials,1995:484-501. |
| [5] | SADANANDA K;VASUDEVAN A K.Short crack growth behavior[A].Philadelphia (PA):American Society for Testing and Material,1997:301-316. |
| [6] | K. Sadananda;A. K. Vasudevan .Crack tip driving forces and crack growth representation under fatigue[J].International Journal of Fatigue,2004(1):39-47. |
| [7] | KUJAWSKI D .A fatigue crack driving force parameter with load ratio effects[J].International Journal of Fatigue,2001,23(supl):239-246. |
| [8] | 姚卫星.飞机结构疲劳寿命分析的一些特殊问题[J].南京航空航天大学学报,2008(04):433-441. |
| [9] | 贾敬华,李亚智,肖健.YB-MD-3有机玻璃的疲劳裂纹扩展特性研究[J].航空材料学报,2006(05):109-112. |
| [10] | GB/T 6398.金属材料疲劳裂纹扩展速率试验方法[S].,2000. |
| [11] | FORMAN R G;KEARNEY V E;ENGLE R W .Numerical analysis of crack propagation in cyclic-loaded structures[J].Journal Basic Engineering,1967,89:459-464. |
| [12] | DINDA S;KUJAWSKI D .Correlation and prediction of fatigue crack growth for different R-ratios using Kmax and △K+ parameters[J].Engineering Fracture Mechanics,2004,71:1779-1790. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%