采用微弧氧化和喷涂二硫化钼基润滑材料并在150 ～200℃固化2h左右的工艺,在铝合金表面制备了低摩擦系数的复合润滑膜.研究了复合润滑膜的结构与性能对摩擦系数的影响.结果表明,去除微弧氧化膜的表面疏松层获得以γ-Al2O3为主的致密硬化层,使其表面硬度明显提高,并且显著降低复合润滑膜的摩擦系数.微弧氧化层的硬度与载荷大小是影响摩擦系数的主要因素,摩擦系数稳定在0.05～0.08,复合润滑膜制备工艺对基材性能影响较小.
参考文献
| [1] | 袁洋,罗状子,田军.铝合金表面微弧氧化耐磨润滑涂层[J].材料保护,2002(05):4-6. |
| [2] | A. L. Yerokhin;A. A. Voevodin;V. V. Lyubimov;J. Zabinski;M. Donley .Plasma electrolytic fabrication of oxide ceramic surface layers for tribotechnical purposes on aluminium alloys[J].Surface & Coatings Technology,1998(3):140-146. |
| [3] | Krishna LR.;Somaraju KRC.;Sundararajan G. .The tribological performance of ultra-hard ceramic composite coatings obtained through microarc oxidation[J].Surface & Coatings Technology,2003(0):484-490. |
| [4] | 辛世刚,宋力昕,赵荣根,胡行方.铝基复合材料微弧氧化陶瓷膜的组成与性能[J].无机材料学报,2006(01):223-229. |
| [5] | XUEW;WANG C;TIANH et al.Corrosion behaviors and galvanic studies of micro arc oxidation films on A1-Zn-MgCu alloy[J].Surface and Coatings Technology,2007,201:8695-8701. |
| [6] | 熊仁章,盛磊,郭洪光.铝合金微弧氧化陶瓷层的耐磨性能[J].兵器材料科学与工程,2000(03):23-26. |
| [7] | 薛群基.铝质材料的摩擦学表面改性[J].表面工程,1997(02):7. |
| [8] | 郭清兵,袁海兵,李翠金,肖乃玉.自润滑型铝合金硬质阳极氧化膜的摩擦磨损性能[J].表面技术,2010(02):21-23,37. |
| [9] | 沈德久,王玉林,卢立红,田新华,杨万和.铝合金表面微弧氧化自润滑陶瓷覆层[J].材料保护,2000(05):51-52. |
| [10] | 薛文斌,华铭,杜建成,田华,施修龄.LC4超硬铝微弧氧化膜的生长及表征[J].航空材料学报,2008(02):34-38. |
| [11] | 沈洁,陈润斋,朱昌琳.固体膜润滑剂在飞船机构中的应用研究[J].航空材料学报,2006(03):192-195. |
| [12] | SIMMONDS M C;SAVAN A;PFL(U)GER E et al.Mechanical and tribological performance of MoS2 co-sputtered composites[J].Surface and Coatings Technology,2000,126:15-24. |
| [13] | 林春元 .二硫化钼的润滑机理[J].中国钼业,1993,45(02):40-45. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%