针对15-5PH钢材料进行了变形工艺实验研究;实验结果表明:当变形量大于30%时,锻件得到了均匀、细小的等轴晶粒组织;随着变形量的增加,硬度值先升后降,但变化幅度不大,锻件硬度变化范围为HB=314～322;锻件的纵向、横向力学拉伸性能差别较小;纵向室温拉伸性能随着变形量的增加,抗拉强度呈现出下降的趋势.而横向室温抗拉强度随着变形量的增加呈现出"波浪"起伏的现象;随着变形量的增加,冲击性能呈现增加的趋势,而纵向冲击性能高于横向冲击性能.
参考文献
| [1] | 王敏,孙利军,姚长贵,廖洪军.冶炼工艺对15-5PH钢质量影响[J].热处理技术与装备,2008(04):32-36. |
| [2] | 戴秀梅,何枫.高强度沉淀硬化不锈钢在飞上应用[J].航空材料学报,2003(z1):280-280. |
| [3] | Habibi Bajguirani H R .The effect of ageing upon the micro-structure and mechanical properties of type 15-SPH stainless steel[J].Materials Science and Engineering,2002,A338:142-159. |
| [4] | Kamila Amato de Campos;Celso Yoshino;Luis Rogerio de Oliveira Hein .Fractal behavior throughout stretch zone of 15-5PH steel under elastic-plastic loading conditions[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2009(1/2):37-41. |
| [5] | A. Abad;M. Hahn;O.S. Es-Said .Corrosion of 15-5PH H1025 stainless steel due to environmental conditions[J].Engineering failure analysis,2010(1):208-212. |
| [6] | M. Aghaie-Khafri;F. Adhami .Hot deformation of 15-5 PH stainless steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(4/5):1052-1057. |
| [7] | 胡南红,高军波,宋湘萍.15-5PH不锈钢气瓶热处理工艺改进[J].金属热处理,2007(01):76-76. |
| [8] | 叶冰.热处理工艺对0Cr15Ni5Cu2Ti钢性能的影响[J].特钢技术,2001(01):47-50. |
| [9] | 赵莉萍,杨慧,李慧琴.固溶处理和时效对17-4PH沉淀硬化不锈钢组织性能的影响[J].特殊钢,2003(04):24-25. |
| [10] | 胡南红.时效工艺对新型不锈钢零件尺寸稳定性的影响[J].热加工工艺,2007(08):67-68. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%