采用扫描式双喷嘴喷射成形装置制备了大尺寸GH4169沉积坯,经热等静压和热模锻得到了直径600mm的模锻件.研究了直接时效(DA)热处理对喷射成形GH4169合金的显微组织和力学性能的影响.结果表明:直接时效喷射成形GH4169合金晶粒细小均匀,晶粒度在ASTM10左右,其第二相主要有δ相、碳氮化物、γ''相和γ'相.与喷射成形标准热处理态和常规变形直接时效态GH4169合金相比,直接时效喷射成形GH4169合金的拉伸和持久性能较高.
参考文献
[1] | G. ZHANG;Z. LI;Y. ZHANG .Modeling the Deposition Dynamics of a Twin-Atomizer Spray Forming System[J].Metallurgical and Materials Transactions, B. Process metallurgy and materials processing science,2010(2):303-307. |
[2] | Lee Shaw;Claus Spiegelhauer .SPRAY FORMING LARGE DIAMETER SPECIAL STEEL BILLETS[J].International Journal of Powder Metallurgy,1997(3):31-36. |
[3] | A Leatham .Spray forming technology[J].Current Advances in Materials and Processes,1996,8:31. |
[4] | 孙剑飞;沈军;曹福洋 .喷射成形镍基高温合金的研究进展[J].材料导报,1999,13(02):10一12. |
[5] | Yunfeng Yang;Simo-Pekka Hannula .Development of precision spray forming for rapid tooling[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):63-68. |
[6] | W T Carter;M G Benz;J K Browning.Clean Metal Spray Forming[A].Minerals,Metals & Materials Society,1997 |
[7] | P D Prichard;R P Datal.Spraycast-X superalloy for aerospace applications[A].TMS,Warrendale PA,1992:205-214. |
[8] | A C Cabralm;A L Haynes.Evaluation of Spray Formed Nickel Base Superalloys for Gas Turbine Engine Components[A].Bltimore,U.S.A,1999 |
[9] | 许文勇;李周;张国庆.喷射成形GH4169合金模锻件研究[J].动力与能源用高温结构材料,2007:139. |
[10] | 张国庆,李周,田世藩,颜鸣皋.喷射成形高温合金及其制备技术[J].航空材料学报,2006(03):258-264. |
[11] | Hui-Yun Bor;Chao-Nan Wei;Huu Tri Nguyen.Aging effects on the γ' and γ" precipitates of Inconel 718[A].Minerals,Metals & Materials Society,2010:679-688. |
[12] | K Lohnert;F Pyczak.Microstructure evolution in the nickel base superalloy AIIVAC 718plus[A].Minerals,Metals & Materials Society,2010:877-891. |
[13] | 《中国航空材料手册》编辑委员会.中国航空材料手册:第2卷变形高温合金铸造高温合金[M].北京:中国标准出版社,2002 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%