采用超声疲劳试验技术,研究了DZ125定向凝固高温合金在频率20kHz、载荷比R=-1下的超高周疲劳失效行为.结果表明:DZ125合金在循环周次大于108下仍发生了疲劳断裂;扫描电镜观察表明,DZ125合金的超高周疲劳裂纹均起源于试样的表面,经疲劳断口定量计算,超高周疲劳的萌生寿命约占总寿命的97.3%;电子背散射衍射(EBSD)分析表明,在超声振动应力的作用下,DZ125合金晶体发生了旋转,外加应力幅越大,晶体旋转的角度会略微增大,疲劳变形区域也略微增大,接近疲劳瞬断区的变形层深度最低;超高周疲劳试验结果经频率修正后,S-N曲线与常规低频疲劳的S-N曲线能很好地衔接.
参考文献
| [1] | J.Z. Yi;C.J. Torbet;Q. Feng;T.M. Pollock;J.W. Jones .Ultrasonic fatigue of a single crystal Ni-base superalloy at 1000℃[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1/2):142-149. |
| [2] | Q. Chen;N. Kawagoishi;Q.Y. Wang .Small crack behavior and fracture of nickel-based superalloy under ultrasonic fatigue[J].International Journal of Fatigue,2005(10/12):1227-1232. |
| [3] | Chu Zhaokuang;Yu Jinjiang;Sun Xiaofeng;Guan Hengrong;Hu Zhuangqi .High cycle fatigue behavior of a directionally solidified Ni-base superalloy DZ951[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):355-361. |
| [4] | 张栋;钟培道;陶春虎.失效分析[M].北京:国防工业出版社,2005 |
| [5] | 刘新灵;张峥;陶春虎.疲劳断口定量分析[M].北京:国防工业出版社,2010 |
| [6] | 王弘 .[D].成都:西南交通大学,2004. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%