采用三种β热处理制度对TC4-DT钛合金板材进行热处理,调整合金的显微组织和损伤容限性能.利用金相显微镜对不同热处理制度下合金的片层组织特征参数进行观察,分析了不同片层组织对合金疲劳裂纹扩展速率的影响.结果表明,粗片层组织的疲劳裂纹扩展速率在近门槛区对组织比较敏感;在Paris区,细片层组织具有较低的疲劳裂纹扩展速率,随着片层厚度的增加,裂纹扩展速率加快;合金在β区短时保温具有更好的综合性能.
参考文献
| [1] | 曹春晓.选材判据的变化与高损伤容限钛合金的发展[J].金属学报,2002(z1):4-11. |
| [2] | JARFALL L .Verification of the damage tolerance of a fighter air craft[J].fatigue,1994,16:67-74. |
| [3] | Lane Lineberger .Titanium aerospace alloy[J].Advanced Materials & Processes,1998(5):45-46. |
| [4] | YODER G R;COOLEY L A;BOYER R R.Microstructure fracture toughness and fatigue crack growth rate in titanium alloys[A].,1987:209. |
| [5] | NIINOMI M;AKAHORI T;FUNAGA K I.Fatigue behavior of titanium alloys[M].Chicago:TMS,1998:307. |
| [6] | SHADEMAN S;SINHA V .An investigation of short fatigue crack growth in Ti-6A1-4V with colony microstructures[J].Mechanics of Materials,2004,36:161-175. |
| [7] | PHELPS H R;WOOD J R.Correlation of Mechanical Properties and Microstructures of Ti-6Al-2Sn-2Zr-2Mo-2Cr-0,25 Si Titanium Alloy[A].Minerals,Metals & Materials Society,1992:193-199. |
| [8] | TERLINDE G;RATHIEN H J;SCHWALB K H .Micro-structure and fracture toughness of the aged β-Ti alloy Ti-10V-2Fe-3Al[J].Metallurgical Transactions A,1988,19:1037-1049. |
| [9] | DURRT N.Titanium for damage tolerance application on A380[A].Hamburg:TMS,2003:2667-2671. |
| [10] | AMS 4905A.Titanium alloy.damage tolerant grade plate 6Al-4V beta annealed[S].USA:Society of Auto motive Engineers,1988. |
| [11] | 曹春晓.钛合金的新型β热处理工艺-BRCT热处理工艺[J].航空制造技术,1996(12):14-16. |
| [12] | 朱知寿;王庆如;王新南 等.一种钛合金准β热处理工艺[P].中国:200410090864.3,2005. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%