采用TIG焊对1.3mm厚的MGH956合金进行原位合金化焊接,对比研究了未添加,添加质量分数为2％,4％和6％的Y2O3对焊缝显微组织及力学性能的影响.结果表明:添加Y2O3后的焊缝组织以等轴晶为主,焊缝晶粒细小均匀,没有明显的金属氧化物聚集现象,并且有新的增强相颗粒析出.Y2O3的添加不仅细化了晶粒,还提高了接头的显微硬度和抗拉强度,从而改善了焊接接头的力学性能.Y2O3添加量为4％时接头抗拉强度最高,平均抗拉强度为605MPa,达到母材的84％.
参考文献
| [1] | Ukai S.;Fujiwara M. .Perspective of ODS alloys application in nuclear environments[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2002(Pt.a):749-757. |
| [2] | Kimura A;Kasada R;Kohyama A;Tanigawa H;Hirose T;Shiba K;Jitsukawa S;Ohtsuka S;Ukai S;Sokolov MA .Recent progress in US-Japan collaborative research on ferritic steels R&D[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2007(a):60-67. |
| [3] | B. van der Schaaf;F. Tavassoli;C. Fazio;E. Rigal;E. Diegele;R. Lindau;G. LeMarois .The development of EUROFER reduced activation steel[J].Fusion engineering and design,2003(1/4):197-203. |
| [4] | 彭顺米;吴承建;胡本芙 等.氧化物弥散强化铁素体型合金的研究[J].金属热处理学报,1997,18(03):101-106. |
| [5] | 胡本芙;彭顺米;吴承建 等.氧化物弥散强化铁素体钢(ODS)再结晶行为的研究[J].金属热处理学报,1999,20(01):12-17. |
| [6] | 淮军锋,郭万林,李天文,袁鸿,姜维.氧化物弥散强化高温合金MGH956的基本焊接性研究[J].材料工程,2008(09):52-55. |
| [7] | 张胜,侯金保,郭德伦,张蕾.MGH956合金TLP连接机理及接头组织分析[J].焊接学报,2004(03):43-47. |
| [8] | 薛海涛,李建国,李俊岳,王宝森.焊条药皮中稀土氧化物向焊缝中过渡机制的研究[J].中国稀土学报,2003(05):580-583. |
| [9] | 朱元凯;洪彦若;彭惰强.稀土氧化物渣系对高硫铁水脱硫预处理的研究[J].稀土,1983(04):9-13. |
| [10] | 苏锵.稀土化学[M].郑州:河南科学出版社,1993 |
| [11] | 赵兴科.稀土对钢焊缝组织的影响[J].热加工工艺,1997(05):6. |
| [12] | 陈剑虹.不锈钢焊接冶金学及焊接性[M].北京:机械工业出版社,2008:8. |
| [13] | Olga Fabrichnaya;Hans Jurgen Seifert;Thomas Ludwig .The assessment of thermodynamic parameters in the Al_2O_3-Y_2O_3 system and phase relations in the Y-Al-O system[J].Scandinavian Journal of Metallurgy,2001(3):175-183. |
| [14] | 杨军,吴鲁海,茅及放.低合金高强钢焊缝熔敷金属强韧化机理[J].焊接学报,2006(03):86-90. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%