采用应变控制方法,测试了TC4钛合金电子束焊接接头及母材低周疲劳性能,记录并比较了不同位置处的载荷-应变曲线,利用扫描电镜观察分析了低周疲劳断裂方式及断口形貌.研究结果表明:在高应变条件下,由于焊接接头区塑性变形能力较差,其低周疲劳寿命低于母材,低应变条件下,母材与焊接接头低周疲劳寿命相当；低周疲劳试样最终失效断裂均发生在母材区,但焊接接头区也存在明显表面裂纹,这与焊接接头区具有较高的强度、抗塑性变形能力及抗疲劳裂纹扩展能力有关.
参考文献
| [1] | SURESH D M;MOHANDAS T .A comparative evaluation of friction and electron beam welds of near-a titanium alloy[J].Materials & Design,2010,31(04):2245-2252. |
| [2] | YUNG W K C;RALPH B;LEE W B et al.An investigation into welding parameters affecting the tensile properties of titanium welds[J].Journal of Materials Processing Technology,1997,63(1/2/3):759-764. |
| [3] | K. Prasad Rao;K. Angamuthu;P. Bala Srinivasan .Fracture toughness of electron beam welded Ti6Al4V[J].Journal of Materials Processing Technology,2008(1-3):185-192. |
| [4] | Oh J.;Kim NJ.;Lee S.;Lee EW. .Correlation of fatigue properties and microstructure in investment cast Ti-6Al-4V welds[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):232-242. |
| [5] | 李行志,胡树兵,肖建中,王亚军,李清华,籍龙波.TA15钛合金电子束焊接接头不同区域的疲劳裂纹扩展行为研究[J].航空材料学报,2010(01):52-56. |
| [6] | 许鸿吉,尹丽香,李晋炜,谢明.TC4钛合金电子束焊接接头组织和性能[J].焊接学报,2005(11):43-46. |
| [7] | 李清华,胡树兵,李行志,肖建中,王亚军,刘昕,籍龙波.TC4钛合金焊接接头组织不均匀性与疲劳性能[J].材料工程,2010(01):62-68. |
| [8] | 吴会强,冯吉才,何景山,张秉刚.电子束焊接Ti-6AI-4V接头断裂行为机制[J].焊接学报,2004(04):59-62. |
| [9] | 刘鹏涛,赵秀娟,刘昕,齐健,陈春焕,王亚军,任瑞铭.氢对TC4钛合金电子束焊接头疲劳裂纹扩展速率的影响[J].航空材料学报,2011(03):52-55. |
| [10] | 吴会强,冯吉才,何景山,张秉刚.Ti-6Al-4V电子束焊接焊缝区域精细组织特征[J].航空材料学报,2005(03):21-24. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%