采用透射电镜、晶间腐蚀、剥落腐蚀实验和极化曲线测试等手段,研究经不同温度和时间时效处理后的2124铝合金预拉伸厚板的微观组织演变,并分析时效处理对合金腐蚀性能的影响.结果表明,随着时效温度的升高或时效时间的延长,合金晶内析出相由S'相向S相转变,析出相数量相逐渐增多,尺寸增大,合金晶界析出相呈链状分布且发生粗化,晶界附近出现无沉淀析出带并宽化;合金抗晶间腐蚀和剥落腐蚀能力减弱,腐蚀敏感性提高,合金的腐蚀倾向增大,腐蚀速率也呈增大的趋势.在时效过程中S'析出相、晶界析出相和无沉淀析出带的变化是影响合金预拉伸厚板腐蚀行为的主因.
参考文献
| [1] | 王祝堂;田荣璋.铝合金及其加工手册[M].长沙:中南大学出版社,2000 |
| [2] | 曾渝,尹志民,潘青林,郑子樵,刘志义.超高强铝合金的研究现状及发展趋势[J].中南工业大学学报(自然科学版),2002(06):592-596. |
| [3] | 刘兵,彭超群,王日初,王小锋,李婷婷.大飞机用铝合金的研究现状及展望[J].中国有色金属学报,2010(09):1705-1715. |
| [4] | 裴和中,尹作升,张国亮,刘远勇.2024与2124铝合金电偶腐蚀行为的对比研究[J].中国腐蚀与防护学报,2012(02):133-136. |
| [5] | S.P. Knight;M. Salagaras;A.M. Wythe;F. De Carlo;A.J. Davenport;A.R. Trueman .In situ X-ray tomography of intergranular corrosion of 2024 and 7050 aluminium alloys[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2010(12):3855-3860. |
| [6] | 张新明,龚敏如,李慧中,陈明安,周卓平.2519铝合金薄板在不同时效状态的抗晶间腐蚀能力[J].中南大学学报(自然科学版),2004(03):349-352. |
| [7] | 李丽洁.Al-Cu-Mg铝合金的腐蚀损伤与防腐措施[J].腐蚀科学与防护技术,2004(05):341-343. |
| [8] | 赵麦群;雷阿丽.金属的腐蚀与防护[M].北京:国防工业出版社,2002 |
| [9] | 尹作升,裴和中,张国亮,刘远勇.热处理制度对2024铝合金晶间腐蚀和抗拉强度的影响[J].腐蚀与防护,2011(02):107-108,127. |
| [10] | 刘瑶琼,郑子樵,李世晨,林莉,黄裕金.高Cu/Mg2×××系铝合金的微观组织与晶间腐蚀行为[J].中国有色金属学报,2011(12):3057-3063. |
| [11] | Sheng YANG;Danqing YI;Sujuan YAO .Exfoliation Corrosion Behavior of 2524 Aluminum Alloy[J].Materials Science Forum,2007(Pt.2):1159-1162. |
| [12] | C. -M. Liao;J. M. Olive;M. Gao;R. P. Wei .In-situ monitoring of pitting corrosion in aluminum alloy 2024[J].Corrosion: The Journal of Science and Engineering,1998(6):451-458. |
| [13] | 王昌臻,潘清林,何运斌,邹亮,尹志民,聂波,何振波.2124铝合金热轧厚板的热处理制度[J].中南大学学报（自然科学版）,2007(03):386-393. |
| [14] | Smith GW. .Precipitation kinetics in solutionized aluminum alloy 2124. Determination by scanning and isothermal calorimetry[J].Thermochimica Acta: An International Journal Concerned with the Broader Aspects of Thermochemistry and Its Applications to Chemical Problems,1998(1):7-23. |
| [15] | WEI R P;LIAO C M;GAO M .A transmission electron microscopy study of constituent-particle-induced corrosion in 7075-T6 and 2024-T3 aluminum alloys[J].Metallurgical and Materials Transactions A,1998,29:1153-1160. |
| [16] | J.A. DeRose;T. Suter;A. Balkowiec;J. Michalski;K.J. Kurzydlowski;P. Schmutz .Localised corrosion initiation and microstructural characterisation of an Al 2024 alloy with a higher Cu to Mg ratio[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2012(Feb.):313-325. |
| [17] | 龚静,汪明朴,张茜,盛晓菲,杨文超,李周.RRA处理对1973铝合金晶间腐蚀与剥蚀的影响[J].中南大学学报（自然科学版）,2012(07):2520-2527. |
| [18] | 赵凯,尹志民,段佳琦,邓英.时效处理工艺对1975合金腐蚀性能的影响[J].中国腐蚀与防护学报,2013(02):153-158. |
| [19] | 王昌臻 .2124铝合金热处理制度与腐蚀行为的研究[D].中南大学,2007. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%