介绍了核电站蒸汽发生器传热管Fe-Cr-Ni合金、特别是800合金的碱性应力腐蚀破裂,总结了材质成分、热处理、应力、冷加工、环境和电化学等因素对Fe-Cr-Ni合金的碱性应力腐蚀破裂的影响,并归纳了预测应力腐蚀破裂敏感电位的方法.
参考文献
| [1] | 石原只雄;丁亚平 .轻水堆核电站腐蚀损伤极其对策[J].核科学与工程,1991,11(03):226-238. |
| [2] | 丁亚平 .轻水堆一回路压力边界部件的腐蚀问题[J].核电工程与技术,1991,4(03):25-33. |
| [3] | Park In-Gyu.Effect of compressive residual stress on the PWSCC behavior of alloy 600TT SG tubings[A].Sendai Japan,1999 |
| [4] | Z. Fang;R. W. Staehle .Effects of the valence of sulfur on passivation of alloys 600, 690, and 800 at 25℃ and 95℃[J].Corrosion: The Journal of Science and Engineering,1999(4):355-379. |
| [5] | Staehle R W.Chemistry and electrochemistry of corrosion and stress corrosion cracking: A Symposium Honoring the Contributions of Staehle R W[A].A publication of TMS,ISBN number 0-87339-478-x,2001:4. |
| [6] | Cels J R .Caustic stress corrosion cracking studies at 288℃ using the straining electrode technique-comparison of alloy 600 alloy 800 and type 304 stainless steel[J].Corrosion,1978,34(06):198-209. |
| [7] | Park Y S;Galvele J R;Agrawal A K et al.Stress corrosion cracking and anodic behavior of AISI 304 stainless inconel 600 and incoloy 800 straining in bioling NaOH solutions[J].Corrosion,1978,34(12):413-418. |
| [8] | Wilson I L;Pement F W;Aspden R G.Caustic stress corrosion behavior of Fe-Ni-Cr nuclear steam generator tubing alloys[J].Nuclear Technology,1976:70-84. |
| [9] | 朱自勇,魏翔云.不同材料高温碱液中的腐蚀行为[J].腐蚀科学与防护技术,1991(01):1. |
| [10] | 杨武;孔德生;吕战鹏 等.镍基合金传热管超胀条件下评审依据的研究(腐蚀实验)."八五"国家重点科技攻关(子专题)项目[Z].,1997. |
| [11] | PATHANIA R S;Cleand R D .The effect of thermal treatments on stress corrosion cracking of alloy-800 in caustic enviroment[J].Corrosion,1985,41(10):575-581. |
| [12] | 黄德伦;孔德生;杨武 .冷加工对800合金抗碱性应力腐蚀破裂的影响[J].腐蚀与防护,1997,18(06):249-252. |
| [13] | HicklingJ;Wieling N .Electrochemical aspects of the stress corrosion cracking of Fe-Cr-Ni alloys in caustic solutions[J].Corrosion Science,1978,20:269-279. |
| [14] | Ding Yaping;Shinobu Matsushima;Shunji Sato et al.Effect of surface treatments on stress corrosion cracking of alloy 800 in caustic solutions[J].Boshoku,1990,39:125-131. |
| [15] | 孔德生;杨武;赵国珍 等.800合金的碱性应力腐蚀破裂Ⅱ硫代硫酸盐的影响[J].中国腐蚀与防护学报,1997,17(04):181. |
| [16] | Castano-Marin ML;Gomear-Briceno D;Hernandez-Arroyo F.Influence of lead contamination of the stress corrosion resistance of Nickel alloys[A].San Diego,CA:1993,(Minerals Metals Materials in Society,Warrendales):189. |
| [17] | 华惠中,黄春波,吕战鹏,杨武.800、600和690合金的铅致应力腐蚀破裂[J].腐蚀与防护,2001(11):483-488. |
| [18] | Parkins R N;Holyrod N T H .[J].Corrosion,1982,38:245. |
| [19] | Yang Wu;Lu Z P;Huang D L et al.Caustic stress corrosion cracking of Nickel-rich ChromiumBearing Alloys[J].Corrosion Science,2001,43(05):963-977. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%