研究了在室温～100℃范围内,含2%HCl的氩气氛中温度对铀表面离子镀铝层腐蚀行为的影响.结果表明,随温度升高,铝镀层抗HCl腐蚀能力下降;与金属铝相比,铝镀层钝化能力增强,抗HCl腐蚀能力优于金属铝和铀,主要表现为氧化腐蚀和氯化腐蚀;同时,与金属铝相似,HCl气体加剧了残余气氛对铝镀层的氧化腐蚀.
参考文献
| [1] | Wang X L;Fu Y B;Xie R S .Surface chemical behavior of triuranium octaoxide in the atmospheres of carbon monoxide and hydrogen[J].Nucl Mater,1998,257:287. |
| [2] | RICHIE A G .The kinetics and mechanism of the uranium oxygen-water vapor reaction between 40 and 100℃[J].Nucl Mater,1986,139:121. |
| [3] | William L M;Jane A L;Robert J H et al.An examination of the initial oxidation of a uranium-base alloy (U-14.1 at%Nb) by O2 and D2O using surface-sensitive technigues[J].Applied Surface Science,1999,150:73. |
| [4] | Totemeier TC. .Characterization of uranium corrosion products involved in a uranium hydride pyrophoric event[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2000(2/3):301-311. |
| [5] | BAKER L;Bingel J D .The kinetics of oxidation of uranium between 300 and 625℃[J].Journal of Nuclear Materials,1986,120:11. |
| [6] | Martz T;Yamada T .Oxidation of U-20at%Zr alloy in air at 423～ 1063℃[J].Journal of Nuclear Materials,1993,199:143. |
| [7] | 陆春海;郎定木;蒋春丽.腐蚀科学与防腐蚀工程技术新进展:铀在干燥HCl气氛中的腐蚀行为研究[M].北京:化学工业出版社,1999:69. |
| [8] | Paul J;F M Hoffman .Decomposition of H2O on clean and oxidized Al(100)[J].Physical Chemistry,1986(90):5321. |
| [9] | Fontaine J M;Lee-deacon O;Duraaud J P .Electron beam effects on oxygen exposed aluminum surfaces[J].Surface Science,1982,122:40. |
| [10] | Taizo Sasaki;Takahisa Ohno .Dissociation process of O2 on the Al (111) surface[J].Surface Science,1999,433-435:172. |
| [11] | Bargeron C B;Nall B H .An electron energy loss study on aluminum single crystals exposed to carbon monoxide[J].Surface Science,1982,119:L319. |
| [12] | Chen G;Lou H .Oxidation behavior of sputtered NiCr-Al-Ti nanocrystalline coating[J].Surface and Coatings Technology,2000,123:92. |
| [13] | 傅广艳,管恒荣,牛焱,李远士,赵泽良,吴维(山文).溅射Cu-Cr合金微晶涂层的氧化[J].金属学报,2000(03):279-281. |
| [14] | Goltson V A .Foundamentals of hydrogen treatment of materials and its classification[J].Journal of Hydrogen Energy,1997(22):119-124. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%